1.  Charge transport mechanisms and memory effects in amorphous TaNx thin films 
Nanoscale Research Letters  2013;8(1):432.
Amorphous semiconducting materials have unique electrical properties that may be beneficial in nanoelectronics, such as low leakage current, charge memory effects, and hysteresis functionality. However, electrical characteristics between different or neighboring regions in the same amorphous nanostructure may differ greatly. In this work, the bulk and surface local charge carrier transport properties of a-TaNx amorphous thin films deposited in two different substrates are investigated by conductive atomic force microscopy. The nitride films are grown either on Au (100) or Si [100] substrates by pulsed laser deposition at 157 nm in nitrogen environment. For the a-TaNx films deposited on Au, it is found that they display a negligible leakage current until a high bias voltage is reached. On the contrary, a much lower threshold voltage for the leakage current and a lower total resistance is observed for the a-TaNx film deposited on the Si substrate. Furthermore, I-V characteristics of the a-TaNx film deposited on Au show significant hysteresis effects for both polarities of bias voltage, while for the film deposited on Si hysteresis, effects appear only for positive bias voltage, suggesting that with the usage of the appropriate substrate, the a-TaNx nanodomains may have potential use as charge memory devices.
PMCID: PMC4016540  PMID: 24134740
Nitrides; TaNx thin films; Amorphous semiconductors; Nanoelectronics; Memory effects; Conductive-AFM
2.  Long-term oxidization and phase transition of InN nanotextures 
Nanoscale Research Letters  2011;6(1):387.
The long-term (6 months) oxidization of hcp-InN (wurtzite, InN-w) nanostructures (crystalline/amorphous) synthesized on Si [100] substrates is analyzed. The densely packed layers of InN-w nanostructures (5-40 nm) are shown to be oxidized by atmospheric oxygen via the formation of an intermediate amorphous In-Ox-Ny (indium oxynitride) phase to a final bi-phase hcp-InN/bcc-In2O3 nanotexture. High-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, electron energy loss spectroscopy and selected area electron diffraction are used to identify amorphous In-Ox-Ny oxynitride phase. When the oxidized area exceeds the critical size of 5 nm, the amorphous In-Ox-Ny phase eventually undergoes phase transition via a slow chemical reaction of atomic oxygen with the indium atoms, forming a single bcc In2O3 phase.
PMCID: PMC3211480  PMID: 21711908