Voltage control of magnetic anisotropy (VCMA) in magnetic heterostructures is a key technology for achieving energy-efficiency electronic devices with ultralow power consumption. Here, we report the first demonstration of the VCMA effect in novel epitaxial Ru/Co2FeAl(CFA)/MgO heterostructures with interfacial perpendicular magnetic anisotropy (PMA). Perpendicularly magnetized tunnel junctions with the structure of Ru/CFA/MgO were fabricated and exhibited an effective voltage control on switching fields for the CFA free layer. Large VCMA coefficients of 108 and 139fJ/Vm for the CFA film were achieved at room temperature and 4K, respectively. The interfacial stability in the heterostructure was confirmed by repeating measurements. Temperature dependences of both the interfacial PMA and the VCMA effect were also investigated. It is found that the temperature dependences follow power laws of the saturation magnetization with an exponent of ~2, where the latter is definitely weaker than that of conventional Ta/CoFeB/MgO. The significant VCMA effect observed in this work indicates that the Ru/CFA/MgO heterostructure could be one of the promising candidates for spintronic devices with voltage control.
Achieving a sufficient voltage control of magnetic anisotropy (VCMA) in magnetic heterostructures is of particular importance for realizing energy-efficiency electronic devices with ultralow power consumption, such as voltage-torque magnetoresistive random access memories (MRAMs)1,2 and low power logic LSIs3,4. By using voltage-controlled magnetization switching, the power consumption for manipulating a bit cell is proposed to be ~1fJ, which is two orders of magnitude lower than ~0.1pJ in the spin transfer torque (STT) technology5. Since magnetic tunnel junctions (MTJs) are key building blocks for high-performance spintronic devices6, the voltage control of magnetization switching in MTJs has greatly promoted the development of the VCMA technology to practical applications7,8,9,10,11,12,13,14,15,16,17,18. Recently, a ultralow power consumption of ~6fJ is achieved in state-of-the-art CoFeB/MgO MTJs with voltage-controlled magnetization switching14,15. Regarding the origin of the VCMA effect, several physical mechanisms have been proposed, such as the modulation of spin-orbit interactions by charge accumulation and depletion19, Rashba effect20,21, voltage-induced redox reaction22, and electro-migration23. Designing and exploring materials for realizing a large magnitude of VCMA effect are still in the ascendant. To date, well-engineered CoFeB8,9,10,11,12,13,14,15, CoFe7,16, FeB17, Fe18, and FePt24,25 ultrathin layers combining with MgO insulators have been extensively studied; however, the voltage effect on the change of magnetic anisotropy is still not large enough in the material systems and the bit-error rate is also a challenge for mass products26. In addition, a large VCMA effect with changing magnetic anisotropy of ~5000fJ/Vm was observed in Co/GdOx bilayers by voltage-driven O2− migration22; whereas, the speed of ions migration process is very slow and the endurance and scalability are still under discussion. Therefore, advanced materials are extremely required for further development of voltage-controlled spintronic devices.
Ru/Co2FeAl(CFA)/MgO is a novel magnetic heterostructure exhibiting a large perpendicular magnetic anisotropy (PMA) induced by the CFA/MgO interface27,28,29. A high out-of-plane tunnel magnetoresistance (TMR) ratio of more than 130% was obtained in fully stacked CFA/MgO MTJs on the 4-fold-symetry Ru buffer at room temperature (RT)29. In addition, it was reported that the CFA alloy film can possess a low intrinsic damping constant30, which is greatly advantageous for decreasing bit-error rate for voltage-controlled spintronic devices26. Recently, giant VCMA effect as high as 1000fJ/Vm in the CFA/MgO structure was theoretically proposed by first principles calculations31. However, from an experimental point of view, complicated interface reactions and/or inter-diffusions could occur in practical ultrathin heterostructures, such as boron diffusion in Ta/CoFeB/MgO structures32,33, which is particularly significant for both the interfacial PMA and the VCMA effect. Very recently, the interfacial atomic structures of epitaxial ultrathin CFA/MgO(001) heterostructures were carefully investigated34. Aluminum atoms from the CFA layer significantly interdiffused into MgO, resulting in an Al-deficient Co–Fe–Al/Mg–Al–O structure near the CFA/MgO interface. The magnetization and PMA, as well as VCMA effect, may have been increased by the atomic replacement. Therefore, experimental examination of the VCMA effect in the Ru/CFA/MgO heterostructures is desired for practical spintronic applications, as well as for promoting theoretical investigations on the origin of the VCMA effect.
In this work, we experimentally demonstrate the VCMA effect in Ru/CFA/MgO MTJs. A large coercivity change induced by voltages was observed for the CFA layer in perpendicularly magnetized MTJs (p-MTJs) with the structure of CFA/MgO/CoFeB/Ta/[TbCo/Co]25 where the CFA was a free layer and the CoFeB/Ta/[TbCo/Co]25 composited layer acted as a reference layer. Quantitative analysis of the VCMA effect was performed by utilizing a magnetoresistance measurement in Ru/CFA/MgO/CoFeB MTJs with an orthogonally magnetic configuration35. Large VCMA coefficients of 108 and 139fJ/Vm were achieved for the CFA film in the epitaxial Ru/CFA/MgO structure at RT and 4K, respectively. Interfacial stability in the structure was demonstrated by repeating measurements of the VCMA effect. Also, the dependences of both interfacial PMA and the VCMA effect on temperature were investigated. It is found that both of them follow power laws of saturation magnetization.
Figure 1a illustrates the whole stack structure for the designed p-MTJs. The deposition condition for each layer is also indicated and the positive direction of applied voltage is defined as the electric current flows from top to bottom layers. The composite upper layers with the structure of CoFeB/Ta/[TbCo/Co]25 are as a reference layer since the TbCo alloy was reported to have a large coercivity36, while the 1-nm-thick CFA is a free layer. The utilization of CoFeB/Ta bilayers in the reference layer is to maintain a high TMR ratio by coherent tunneling through the MgO barrier. The tunneling resistance (R) as a function of out-of-plane magnetic field (H) for a patterned p-MTJ with 100-nm-nanoscale in diameter is shown in Fig. 1b. A direct-current (dc) voltage of 1mV was applied to measure the resistance here. A TMR ratio of 65% was achieved with a resistance-area product (RA) of ~175Ω·μm2. The TMR ratio is defined as 100×(RAP–RP)/RP, where RAP (RP) is the resistance of the antiparallel, AP (parallel, P) magnetization state. A sharp resistance change observed in the middle of the full R–H loops indicates that a perfect perpendicular magnetization and coherent switching for the CFA free layer were achieved in the heterostructure. Figure 1c shows the minor loops of normalized TMR as a function of magnetic field at the bias voltages of −800mV, 1mV, and 800mV, respectively. A large change in the switching field (Hs) is observed in the CFA layer when the voltages were applied. For instance, the Hs from P to AP state is −780Oe at 800mV while it becomes −900Oe at −800mV. The ΔHs of 120Oe is modulated by the voltages, which is much larger than that in CoFeB/MgO p-MTJs8. The detailed voltage dependence of Hs for the CFA layer from P (AP) to AP (P) magnetization states is shown in Fig. 1d. The coercivities of the CFA layer at each voltage can be derived by (Hs(AP-to-P)−Hs(P-to-AP))/2. It is found that the coercivity decreases with increasing voltage from negative to positive bias direction. In comparison with previously reported ferromagnetic (FM) layer/MgO systems8,9,10,11,12,13,14,15,16,17,18, it is indicated that one of the main mechanisms for the VCMA effect in the p-MTJ is likely to be charge accumulation/depletion19. The charge accumulation/depletion modulates the electronic occupancy of 3d orbitals in the band structure as well as spin-orbit interactions at the CFA/MgO interface, resulting in the change in effective magnetic anisotropy of the CFA layer. In addition, the maximum current density is calculated to be 4.6×105A/cm2 in the p-MTJ, which indicates STT effect could partially contribute the magnetization switching. The asymmetry of switching fields between positive and negative voltage biases in Fig. 1c and and1d1d may be attributed to the influence of STT effect.
In order to quantitatively evaluate the VCMA effect in the Ru/CFA/MgO heterostructures, we use a method of in-plane magnetoresistance measurement by utilizing an orthogonally magnetized MTJ35. Figure 2a shows the illustration of the MTJ structure in which the CFA layer is perpendicularly magnetized while the CoFeB layer has in-plane magnetic anisotropy. The external magnetic field was applied along the in-plane direction and R–H loops were measured under different voltages. The VCMA effect was estimated by normalizing the measured curves using the minimum (H=10kOe) and maximum (H=0Oe) resistances. Figure 2b shows normalized TMR curves at the voltages of 10,±500, and ±1100mV in the positive magnetic field region. A clear dependence of TMR curves on the bias voltages was observed. Since the influence of the bias voltages on the magnitude of TMR ratio is excluded by the normalizing process, the variation in the TMR curves at different voltages indicates a remarkable VCMA effect on the CFA layer. In addition, the maximum current density is estimated to be 1.1×102A/cm2 in the orthogonally magnetized MTJs. The small current density indicates that the influence of STT effect could be negligible in the devices. The PMA of the CFA films was calculated using the measured R–H curves. The conductance of the MTJ is related to the relative angle θ between the magnetizations of CFA and CoFeB layers, which can be expressed by the equation below,
Here G90° (G0°)=1/R90° (1/R0°) is the conductance of the MTJ in orthogonal (parallel) magnetization configuration. Because the magnetization of CoFeB reference layer is fixed in the film plane, the in-plane component of the magnetization of the CFA layer can be obtained by,
where MS is the saturation magnetization of the CFA film. Furthermore, the PMA energy density Ku can be calculated as,
where μ0 is the permeability of free space and Mnorm. is the Min-plane normalized by Ms. A typical normalized in-plane component of the magnetization is shown in Fig. 2c. The shaded area indicates the magnitude of PMA energy density in which the effective value includes demagnetization, bulk and interface contributions to the system. Figure 2d shows the PMA density per unit area, Kut, as a function of applied electric field for the CFA film. At the negative (positive) bias direction, an increase (decrease) in the Kut with increasing the magnitude of electric field was observed. A clear deviation of linear tendency of the Kut–E curve between positive and negative bias directions was shown. The similar behavior was also observed in the CoFeB/MgO8 and Fe/MgO18 heterostructures. Linear fits were performed independently for the positive and negative bias regions. The slope of 108 (50)fJ/Vm was achieved in the negative (positive) bias direction, which is defined as the coefficient ξ of the VCMA effect in the CFA film. The maximum value is much larger than 33fJ/Vm for the CoFeB film in the Ta/CoFeB/MgO structure10, and comparable to ~100fJ/Vm for the CoFeB film in the Ir/CoFeB/MgO structure13 and for the FeB film in the MgO/FeB/MgO structure17. Also, we were aware of opposite signs of VCMA effect, i.e., the sign of ξ, observed between polycrystalline Ru/CoFeB/MgO and Ta/CoFeB/MgO structures10. Interestingly, the sign of the VCMA effect in this work is opposite to that of the polycrystalline Ru/CoFeB/MgO and is the same as that of the Ta/CoFeB/MgO. The sign of the VCMA effect is expected to be sensitive to the electronic structures near the interfaces of a FM layer. Especially, the electronic structures of nonmagnetic (NM) layers adjacent to the FM layer can determine the signs of the VCMA effect, which had been demonstrated by first principles calculations in Pt/Fe/Pt and Pd/Fe/Pd structures37,38. Therefore, the difference in the ferromagnetic material (CFA and CoFeB) and/or crystal structure (e.g., polycrystalline hcp Ru and single crystalline Ru(023) buffer layers) may be responsible for the discrepancy of the signs. However, the buffer layer dependence of the sign of the VCMA effect, as well as the deviation of the VCMA magnitudes between negative and positive bias regions18, are still under discussions.
Furthermore, we investigated the chemical stability of the interfaces in the Ru/CFA/MgO heterostructure by repeatedly measuring the VCMA effect. Figure 3 shows typical VCMA measurements by applying bias voltages of ±1V back and forth for 300 times. The time interval between two points is one second. The PMA energy density of Kut is calculated at each bias voltage for every time. The inset is a magnified figure for 50-times measurements. The PMA value is well maintained without any decay in the count scale, indicating the crystal structures and interfaces are chemically stable in the Ru/CFA/MgO heterostructure.
Next, we study the temperature dependence of the VCMA effect. Figure 4a shows the applied electric field dependence of Kut at different temperatures. The Kut is calculated by the equation (3) in which the Ms at each temperature was measured as shown in Figure S1 in the Supplementary information. The Ms–T curve was well fitted by the Bloch’s law,
With decreasing temperature, a clear shift of Kut–E curves is shown, indicating an increase in the magnetic anisotropy for the CFA film at low temperatures. The discrepancy in the linear slopes of the Kut–E curves between positive and negative bias regions was still observed in the entire temperature range. Figure 4b shows the interfacial magnetic anisotropy Kut at zero applied electric field as a function of temperature. The solid line indicates a fitted curve by a power law of Ms(T),
It is found that the temperature dependence of Kut is well fitted by the power law with an exponent of γ=2.00±0.08. The result is corresponding with the theoretical prediction of a Ms2(T) dependence for the magnetic anisotropy especially in the material systems with PMA contributed by high spin-orbit interactions39,40. In general, the temperature dependence of uniaxial anisotropy follows Callen-Callen’s Ms3(T) law in a simple ferromagnetic system41. The Ms2(T) power law indicates that the Ru/CFA/MgO system processes a strong spin-orbit interaction where localized moment or two-ion anisotropic exchange makes a main contribution to the temperature dependence of magnetic anisotropy39,40. A similar Ms2(T) dependence was also observed in MgO/CoFeB/Ta heterostructures with interfacial PMA42. Furthermore, we investigate the VCMA coefficient ξ as a function of temperature, as shown in Fig. 4c. The ξposi. (ξnega.) values are derived by linearly fitting the Kut–E curves in the positive (negative) region. A maximum ξ of 139fJ/Vm is achieved at 4K for the negative region. Interestingly, the VCMA coefficient ξnega. decreases with increasing temperature while the ξposi. is nearly independent of the temperature. We fit the temperature dependence of ξnega. using a power law of Ms(T),
The solid line in the Fig. 4c shows a well fitted curve by the power law of Ms(T) with an exponent γ′=1.89±0.29, which is near to the Ms2(T) as the temperature dependence of interfacial magnetic anisotropy. It should be noted that the exponent is definitely smaller than 2.83 in the MgO/CoFeB/Ta system42, which could be attributed to the different spin-orbit coupling behavior in Fe-O hybridization and/or discrepant electronic band structures at the FM/NM interfaces. The effective mechanism for the magnitude of VCMA coefficient is still an open question. The power law fitting could give some insights to the strength of spin-orbit coupling with respect to VCMA. Figure 4d shows the magnetic anisotropy dependence of the VCMA effect. The ξnega. obtained in the negative bias region increases with increasing Kut, whereas the ξposi. for the positive bias region shows a weak magnetic anisotropy dependence. The asymmetric dependence of VCMA coefficient for positive and negative bias voltage is another important feature in the system. The independence of the ξposi. could be related to the origin of the nonlinearity of the VCMA effect. Nonlinear VCMA effects were also reported in several systems in which the possible origins include electronic structures43, Rashba effect21, and strains44. The present temperature dependence in our experiment would provide a significant hint for future studies on the mechanisms of VCMA effects. Theoretical calculations will be strongly required for further understanding of the mechanisms to explain the observed temperature and magnetic anisotropy dependences of the VCMA effect.
In summary, the VCMA effect in the Ru/CFA/MgO heterostructures was experimentally demonstrated. Perpendicularly magnetized MTJs with the structure of CFA/MgO/CoFeB/Ta/[TbCo/Co]25 were fabricated, which exhibited effectively voltage-controlled switching fields for the CFA free layer. Quantitative analysis of the VCMA effect revealed large VCMA coefficients of 108 and 139fJ/Vm for the CFA film in the epitaxial Ru/CFA/MgO structure at RT and 4K, respectively. The chemical stability of the heterostructure was examined by repeating VCMA measurements. It was also found that temperature dependences of both the interfacial PMA and the VCMA effect followed power laws of the saturation magnetization with a material-specific exponent. This study indicates the Ru/CFA/MgO heterostructure could be a promising candidate for spintronic applications with voltage-controlled magnetism.
All the multilayers were deposited by magnetron sputtering in an ultrahigh vacuum system with a base pressure of 3×10−7Pa. The p-MTJ multilayer stack has a structure of MgO(001)-substrate//Ru(40)/CFA(1)/MgO(1.3)/CoFeB(1.5)/Ta(0.45)/[TbCo(0.3)/Co(0.3)]25/Ta(5)/Ru(10) (unit: nm). The Ru layer was post-annealed at 400°C for 30min after deposition in order to form a (023) epitaxial growth for achieving high-performance CFA/MgO bilayers. The bottom stack of Ru/CFA/MgO/CoFeB/Ta was annealed at 325°C for 1h before depositing TbCo/Co multilayers for the purpose of obtaining both high TMR and large PMA simultaneously. The TbCo/Co multilayers were deposited at RT by a co-sputtering method from Co and Tb targets. Furthermore, an orthogonally magnetized MTJ stack with the structure of MgO(001)-substrate//Ru(40)/CFA(1)/MgO(2.2)/CoFeB(20)/Ta(5)/Ru(10) (unit: nm) was deposited for quantitative analysis of VCMA effect on the CFA layer. The condition of the deposition was identical to that for p-MTJs. The measurement of Ms at low temperatures was performed using a superconducting quantum interference device (SQUID) magnetometer. All the MTJ stacks were patterned into junctions with electric contacts by electron beam lithography and conventional UV lithography combining with Ar ion milling and lift-off technique. The magneto-electrical transport measurements were performed by a dc four-probe method at RT and low temperatures in a physical property measurement system (PPMS).
How to cite this article: Wen, Z. et al. Voltage control of magnetic anisotropy in epitaxial Ru/Co2FeAl/MgO heterostructures. Sci. Rep. 7, 45026; doi: 10.1038/srep45026 (2017).
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
This work was partly supported by the ImPACT program of the Council for Science, Technology and Innovation (Cabinet Office, Government of Japan) and JSPS KAKENHI Grant Number 16H06332. A part of this work was performed under the Inter-university Cooperative Research Program of Institute for Materials Research, Tohoku University (16K0072).
The authors declare no competing financial interests.
Author Contributions S.M. and K.T. supervised the study. Z.W. and S.M. designed the experiments. Z.W. and H.S. deposited and micro-fabricated the samples. Z.W., T.S. and T.K. carried out the measurements and analyzed the data. Z.W. and S.M. wrote the manuscript with reviewing by H.S., T.S., T.K. and K.T. All authors discussed the results and the manuscript.