Mesoporous silica nanoparticles (MSNs) impregnated with zero-valent Fe (Fe(0)@MCM-41) represent an attractive nanocarrier system for drug delivery into tumor cells. The major goal of this work was to assess whether MSNs can penetrate the blood-brain barrier in a glioblastoma rat model. Synthesized MSNs nanomaterials were characterized by energy dispersive X-ray spectroscopy, measurements of X-ray diffraction, scanning electron microscopy and Mössbauer spectroscopy. For the detection of the MSNs by MR and for biodistribution studies MSNs were labeled with zero-valent Fe. Subsequent magnetometry and nonlinear-longitudinal-response-M2 (NLR-M2) measurements confirmed the MR negative contrast enhancement properties of the nanoparticles. After incubation of different tumor (C6 glioma, U87 glioma, K562 erythroleukemia, HeLa cervix carcinoma) and normal cells such as fibroblasts and peripheral blood mononuclear cells (PBMCs) MSNs rapidly get internalized into the cytosol. Intracellular residing MSNs result in an enhanced cytotoxicity as Fe(0)@MCM-41 promote the reactive oxygen species production. MRI and histological studies indicated an accumulation of intravenously injected Fe(0)@MCM-41 MSNs in orthotopic C6 glioma model. Biodistribution studies with measurements of second harmonic of magnetization demonstrated an increased and dose-dependent retention of MSNs in tumor tissues. Taken together, this study demonstrates that MSNs can enter the blood-brain barrier and accumulate in tumorous tissues.
Glioblastoma multiforme (GBM) is highly aggressive primary brain tumor that is associated with high morbidity and poor prognosis. Despite multimodality treatment approach that currently includes maximal surgical resection, followed by a combination of radiotherapy and/or chemotherapy with temozolomide (TMZ), the median survival does not exceed 15 months1. Targetable nanocarriers for treating malignant gliomas are a unique way to overcome chemotherapeutic levels at target sites devoid of systemic toxicity2. One of the currently available nanocarrier systems are nanoparticles based on silica.
Mesoporous silica-based nanoparticles (MSNs) represent an attractive system for a controlled release of anticancer drugs including chemotherapeutic agents, small interfering RNAs (siRNA), radiotherapy sensitizers3,4,5,6. Numerous studies showed the possibility of efficient drug delivery by MSNs7,8,9,10,11. Thus great immune-stimulating activity in vivo was provided by MSNs, which carried oligodeoxynucleotides (ODN) containing cytosine-guanine (CpG), in comparison to the control free CpG therapeutics, as it was found in the study by Zheng et al.12. For further tumor-specific targeting MSNs could be functionalized with various bioligands13,14,15. In the study by Goel et al. MSNs coated with anti-VEGFR ligand VEGF121 could deliver significantly higher amounts of sunitinib to U87MG when compared with the non-targeted counterparts14. In another study by He et al. it was shown that MSNs coated with seleno-amino acid and conjugated with TAT cell penetrating peptide and transferrin (SeC@MSNs-Tf/TAT) preferentially accumulated in cancer cells due to the receptor-mediated endocytosis15.
Up-to-date studies demonstrated the therapeutic efficacy of MSNs for targeting glioma cells in in vitro experiments. However, the question whether nanoparticles can penetrate the brain-tumor barrier still remained to be elucidated. In a recent work of Huang et al. retention of MSNs was revealed in an orthotopic U87MG glioblastoma model where mesenchymal stem cells were applied for the transportation of the MSNs16. In the present investigations the ability of Fe(0)@MCM-41 nanoparticles for targeting the brain tumor was investigated in the model of orthotopic C6 glioma with application of the magnetic resonance imaging (MRI). Moreover, the study of biodistribution of magnetic nanoparticles was carried out applying the sensitive measurements of second harmonic generation in parallel dc H and weak ac h(t) magnetic fields (NLR-M2)17.
The morphology of the synthesized MSNs was determined by means of scanning electron microscopy (SEM) (Fig. 1). Figure 1B demonstrates clearly the porous structure of the nanoparticles. Their average length constituted 250nm and the average diameters varied from 100 to 150nm. The average diameter of pores constituted 3.3nm (Fig. 1C). Figure 1D shows the nitrogen adsorption isotherm of the calcinated Fe(0)@MCM-41 particles, clearly indicating the increase of the nitrogen absorption with the increase of the pressure. Following incorporation of the zero-valent Fe into the MSNs we could detect the ferrum in the pores though we did not observe the change in the size of the particles. Comparison of spectra of energy dispersive X-ray (EDX) from Fe(0)@MCM-41 nanoparticles and empty MSNs demonstrated the presence of the peak originating from iron (Fig. 1E). X-ray difractometry registered with a time of data collection of 2s pre each step and angle step of 0.01° reveals the crystalline α-Fe phase in the Fe(0)@MCM-41 nanoparticles (Fig. 1G). The presence of zero-valent Fe in samples with the MNSs was supported by subsequent Mössbauer measurements (Fig. 1F). Figure 2A presents the magnetization hysteresis of Fe(0)@MCM-41 which has been obtained in steady field varied within –1T – 1T at room temperature. Saturation magnetization (Ms) constituted 7.4emu/g. To analyze the magnetic state of Fe(0)@MCM-41 particles the NLR setup was applied, registering the magnetic response on second harmonic, M2, (Fig. 2B). Both phase components, ReM2 and ImM2 were recorded simultaneously in dependence on steady field H at varied frequency of field scan, Fsc, and constant T=294K under condition M2 h2 (h – is amplitude of ac field) (Supplementary Fig. S1). The concentration of Fe(0)@MCM-41 was about 0.01mg/ml. The presented signals reveal extremes in a weak H ~100Oe for both phase components ReM2, ImM2, exhibiting inverse signs, and discrepancy in their H-dependencies registered during direct and reverse scannings of steady field H (field hysteresis). The latter decreases with decreasing of Fsc, evidencing its dynamical reason. The listed peculiarities of M2-response are characteristic for that of ensemble of magnetic nanoparticles in single domain regime, which do not interact with each other, near blocking temperature like these of other similar ensembles17. The converse signs of obtained signals in real ReM2 and imaginary ImM2 components suggest respectively the distinct major reasons of their origination: (i) a nonlinear dependence on field of the magnetization of MSN ensemble, M, in ReM2 2M/H2; and (ii) an external field influence on relaxation processes in ImM2 (Γ/H)·(M/H) (here Γ=1/τ is the magnetic relaxation rate). These findings indicated that interaction of Fe(0)-nanoparticles intercalated inside the porous Fe(0)@MCM-41 composite particle is rather weak and they did not form multidomain magnetic system inside single particle.
Internalization and cytotoxicity of the developed MCM-41 and Fe(0)@MCM-41 particles were assessed in rat C6 glioma, human U87 glioblastoma, human leukemia K562 and cervix carcinoma HeLa cells. Rat’s splenocytes and fibroblasts were used as normal tissue cells. Cells were co-incubated for 1, 3, 6, 12, and 24hours with Fe(0)@MCM-41 nanoparticles at different concentrations of Fe (C=1, 10, 50, 150μg/ml). Analysis of confocal microscopy data clearly indicated the accumulation of Fe(0)@MCM-41as well as MCM-41 particles in cytosol of cancer cells as a result of overnight co-incubation (Fig. 3). Indeed, the particles can be seen as surrounding the nucleus as red dots in all cell types on the confocal microscopy images obtained in reflective regime (Fig. 3A). The highest incorporation of the nanoparticles was observed 24hours after co-incubation. The similar dynamics of particles incorporation was also observed when fibroblasts or PBMCs were applied. Subsequent transmission electron microscopy (TEM) of C6 cells indicated the existence of the dense structures in the cytoplasm, well scattering the electrons, which corresponds to MCM-41 and Fe(0)@MCM-41 (Fig. 3C). Cytotoxicity assay demonstrated that Fe(0)@MCM-41 but not MCM-41 nanoparticles did exhibit cytotoxicity towards tumor cells and normal cells (Fig. 4). Thus 12hours following cell exposure to Fe(0)@MCM-41 particles (at 150μg/ml) there was an increase of cytotoxicity up to 40% (Fig. 4A). The cytotoxicity was further increased at time point of 24hours which corresponded to the highest incorporation of particles (confirmed by confocal microscopy). An involvement of reactive oxygen species (ROS) could be the cause for the elevated cell death. Therefore the rate of ROS production was gauged by us in tumor and normal cells both under normal growth conditions and after co-incubation with MCM-41 and Fe(0)@MCM-41 nanoparticles. ROS were tested by applying a fluorescent probe of dichlorodihydrofluorescein diacetate (DCDHF) (Molecular Probes, USA). When MCM-41 particles were applied no considerable growth of ROS production was detected in all tested cells (data not shown). However, the registered ROS production rate was noticeably enhanced in the cells treated with Fe(0)@MCM-41 nanoparticles (Fig. 4B). The increasing depended on the concentration of the Fe, time of co-incubation with nanocarriers as well as cell type.
On day 15 after intracranial injection of C6 cells a random arrangement of all animals was performed between four groups (6 animals in each) by the following way: (1) control group after phosphate-buffer solution (PBS) injection intravenously; (2) I.V. injection of MCM-41; (3) the Fe(0)@MCM-41 injection intravenously by dose of 2.5mg/kg during 24hours; (4) I.V. injection of Fe(0)@MCM-41 by dose of 10mg/kg during 24hours. After intravenous infusion of the particles no obvious side effects were observed (i.e., behavioral changes). Following intravenous administration of Fe(0)@MCM-41 the MR images exhibiting high-resolution were registered (Fig. 5A). The C6 glioma being visible on MR images as hypotensive zone at registration of scans in regime the T1-weighting, became slightly hypertensive on those obtained in the T2-weighted regime. Infusion of the MCM-41 nanoparticles did not lead to the enhancement of the tumor contrast in MR scans. Following Fe(0)@MCM-41 injection the origination in the glioma of the ‘dark’ hypotensive zones was found on the images registered in T2-weighted regimen. The latter became more contrast at application of the FLASH regimen (Fig. 5A). When conjugates were injected by the 10mg/kg dose retention of the MSNs nanoparticles in the tumor was significantly higher compared to the lesser (2.5mg/kg) dose. This enhanced the tumor contrast at applying scans with T2-weighting and Fe(0)@MCM-41 nanoparticles could be detected in patchy pattern of hypotensive zones. Multigradient sequences with T2*-weighting (MSME regimen) have been additionally exploited to estimate T2* values. The determined quantity of T2* was 45±6s−1 in control group. Intravenous injection of Fe(0)@MCM-41 resulted in a decrease of T2* magnitude to 32±3s−1, that was further dropped down to 21±6s−1 (P<0.001) when 10mg/kg dose was used. In the animals treated with MCM-41 without the Fe the T2* values did not significantly differ from that of control group constituting 46±3s−1. Subsequent immunofluorescence staining demonstrated an accumulation of the Fe(0)@MCM-41 in the glioma tissue when dose of 2.5mg/kg was used (Fig. 5B). Nanoparticles localized in the extracellular space in the perivascular zones in the tumor tissue. When particles were injected at dosage of 10mg/kg we observed a significant increase of Fe(0)@MCM-41 retention in the tumor.
Analysis of the Fe(0)@MCM-41 nanoparticles accumulation in the tissue of intact brain of glioma-bearing rodents by NLR-M2 measurements did not indicate the retention of the conjgates in the brain tissue (Fig. 5C). These data suggest that non-magnetic MCM-41 particles do not penetrate also the intact blood-brain barrier. Incorporation of MCM-41 into glioma cells can be qualitatively assessed from in vitro experiments with C6 cells (confocal microscopy and TEM data, Fig. 3A,C). When the tumor samples were obtained from rats treated with dose 2.5mg/kg of the Fe(0)@MCM-41 the incorporation of the latter in tumor can be seen on the immunofluorescent images (Fig. 5B). However, the ReM2 response from tumor only slightly exceeded that from control untreated (or treated with MCM-41) animals (with ratio 1.12; Table 1) and exhibited considerable H-hysteresis (Fig. 5C) similar to this in signal of Fe(0)@MCM-41 in suspension solution (Fig. 2). The data suggest that there is no release of Fe(0) from pores of silica particles followed by oxidation of Fe(0) to Fe3O4 and appearance of non-hysteretic M2(H)-signal like that for 10mg/kg dosage (see below) (Fig. 5C; Table 1). Administration of Fe(0)@MCM-41 at dosage of 10mg/kg enhanced the accumulation of the MSNs in the glioma with subsequent release of Fe(0). Its oxidation was accompanied by increase of the non-hysteretic M2(H)-response (Fig. 5C), which was similar to that of Fe3O4-based nanoparticles used in earlier investigations17,18. The dramatic enhancement (~770-fold) of magnetic nanoparticle accumulation in glioma in comparison to 2.5mg/kg dosage (Table 1) indicated the proportional increase of concentration of Fe(0) released from the MCM-41, since the amplitude of ReM2 NP’s concentration17. The effect of magnetic NPs on contrast of MR images occurred through changing of the relaxation characteristics T1, T2, T2*, which depended on the NPs distribution (Fig. 5A). Biodistribution of magnetic nanoparticles in tissues of treated rodents was assessed by study of nonlinear response in longitudinal geometry of parallel weak ac, h(t)=h·sinωt, and dc, H, magnetic fields, second harmonic of magnetization, M2(H), being registered. Intriguingly, a weak M2(H) signal exhibiting field hysteresis and extremum in a small field H~50Oe was found in some tissues of control non-treated animals (Supplementary Fig. S2). Signals were detected in tissues of tumor, skin, heart and muscle. The latter implies the presence of some magnetic nanoparticles in certain intact tissues. Reasons for this still remain unclear; one may suggest that the latter are presumably involved in a cell metabolism. Control tissue’s M2 signals were always significantly weaker of those from corresponding tissues (including tumor) of MNP-treated animals17. In current study with use of Fe(0)@MCM-41, an exception was detected only for heart tissue, where the amplitudes of these signals were comparable (Supplementary Fig. S2). Following injection of Fe(0)@MCM-41 by dose 2.5mg/kg the relative retention of MNP in tissues and organs increased as follows: tumor<muscle≤heart<brain<lungs<skin<kidney liver<spleen (Table 1). In 24hours after administration of Fe(0)@@MCM-41 at dosage of 10mg/kg the ReM2(H) response enhanced in tumor and in less extent in lungs, as well as the order of relative increase of MNP retention in tissues changed in the following way: muscle≤brain ≈ kidney ≈ heart<skin lungs<tumor<spleen<liver (Supplementary Fig. S3 and Table 1). The interesting peculiarity of obtained M2(H) dependences, which can be seen from this Figure, is their non-hysteretic character in responses from spleen, liver, tumor and slightly hysteretic one from lungs tissue, which corresponds to response of Fe3O4-based magnetic NPs in superparamagnetic regime employed in previous studies17 and differs drastically from hysteretic M2-signal of Fe(0)@MCM-41 in suspension solution (Fig. 2). At the same time the other tissues reveal the rather weak hysteretic response corresponding to that of NP solution and comparable in value with control signals (Supplementary Fig. S1). This suggests that the Si-based shell of composite is destroyed in first group of tissues, as can be expected, releasing the Fe(0) NPs, and the latter is further oxidized to Fe3O4=Fe2O3×FeO state. In lungs, where content of oxygen is higher, the oxidation leads to some larger amount of Fe2O3 as compared to FeO, and we observed some H-hysteresis, since M2 response of the former is characterized by H-hysteresis. Thus the obtained results imply the possible Fe(0) oxidation in case of Fe(0)@MCM-41 particles.
The application of mesoporous nanocarriers in the oncology field opens a promising perspective owing to the ability for transportation of therapeutic agents and their liberation in tumor in a controlled manner19. For the assessment of the biodistribution of MSNs in animal brain tumors Fe(0) was confined into the pores of the nanoparticles. The obtained nanocarriers had the properties of T2-negative contrast enhancers (Figs 1 and and22).
When we applied non-impregnated with Fe(0) MCM-41 nanoparticles we did not observe any cellular toxicity. The obtained results are in accordance with data published recently by Sadeghnia et al. showing that exposure of MSNs to rat pheochromocytoma PC12 cells (1.95–1000μg/mL) did not result in reduction of cell viability. The amount of intracellular reactive oxygen species (ROS) and oxidative DNA damage also did not differ in these nanoparticles20. When Fe(0) was incorporated into the pores of the nanoparticles we observed a subsequent increase of cellular cytotoxicity (Fig. 4). This could be attributed to the oxidative stress induced by glutathione depletion, followed by ROS induction and peroxidation of lipids21. Previously in the work by Watanabe et al. it was shown that Fe3O4 magnetic nanoparticles (MgNPs- Fe3O4) provided the growth of ROS production even at lower concentration (10μg/mL) followed by increase of oxidative damage of DNA, and reduction of the glutathione level; at high concentration (100μg/mL) they caused cell membrane damage22. High ROS levels can subsequently damage cells by disrupting DNA, altering gene transcription that could result in activation of apoptotic pathway23,24,25. Increased amounts of ROS also might damage the mitochondrial DNA (mDNA)26. Furthermore, it was demonstrated that oxidative stress induced by nanoparticles affects cell signaling activating inflammation through NF-κB27. It was found also that Fe(0)@MCM-41 nanoparticles reveal a cytotoxicity which depends on the dose. Similar results were reported previously for silica-coated iron oxide nanoparticles for the primary human macrophages, dendritic cells and A549 human lung adenocarcinoma cells28,29. Subsequent measurement of ROS production confirmed this mechanism in our data set (Fig. 4B). One of the possible solutions for reduction of Fe(0)@MCM-41 toxicity could be the functionalization or coating of the MSNs surface with various ligands including proteins, sugar moieties, hyperbranched poly(ethylene imine), PEG30,31,32. Thus end-capping of MSNs with such natural proteins as bovine serum albumin, gelatin, and lysozyme dramatically reduced the immunotoxicity of nanocomposites31. From the other hand the possibility of Fe(0)@MCM-41 to activate ROS-mediated signaling pathways could be exploited in cancer treatment. Thus, upon irradiation of tumor cells that incorporated SeC@MSNs-Tf/TAT nanoparticles, the latter induced overproduction of ROS inside cells, which activated the mechanisms of apoptosis by activating p53, AKT and MAPKs pathways15. Additional incorporation of the ROS-generating drugs can potentially increase the therapeutic potency of MSNs. In the study by Huang et al. it was shown that micelles of SPIONs which included β-lapachone (β-lap) known to selectively increase ROS production have a significant cytotoxic effect33.
Administration of the Fe(0)@MCM-41 via intravenous injection accompanied by the incorporation of the nanoparticles in the tumor (Fig. 5). Thus we observed a significant retention of the MSNs in the perivascular spaces in the glioma on the cryosections of the tumor (Fig. 5B). This led to the enhancement of the tumor contrast on gradient echo MR images obtained by the T2-weighted scans (Fig. 5A). The MR pattern of MSNs presentation in the tumor was similar to the earlier reported non-specific accumulation of the SPIONs in the C6 glioma34,35,36.
The observed accumulation of the Fe(0)@MCM-41 nanoparticles in the glioma could be explained by the increased blood-brain barrier permeability in the tumor18. Previously it was found that glioma tumors disrupt the connection of astrocytes and brain endothelial cells37. Thus in the study Watkins et al. it was shown that invading along the preexisting blood vessels glioma cells disrupt the astrocytic end-feet attachment from endothelial cells38. Moreover, decreased expression of the tight junction proteins (i.e., occludin) as well as overexpression of aquaporin-4 result in the impairment of the endothelial tight junctions31,39. The abnormalities of tumor tissue architecture and vasculature leakage could also be responsible for the phenomenon of enhanced permeability and retention (EPR) effect40. This effect provides the basis for selective delivery of macromolecular drugs to the site of the solid tumors. Thus Fe(0)@MCM-41 achieve very high local intratumoral concentrations within 24hours after administration (Fig. 6).
One of the conclusions from the obtained data is the possibility of Fe(0)@MCM-41 to reach the brain tumor. The porous structure of MSNs could be applied for the prolonged drug delivery. Thus in the work of Gordon et al. the possibility of prolonged drug dissolution (e.g., acetaminophen, progesterone, stavudine) by MSNs of various formulations was shown41. In another study formulated multifunctional inorganic mesoporous nanocapsules (Fe(3)O(4)@mSiO(2)) demonstrated high efficiency in doxorubicin release42. Intra-tumorally accumulated MSNs could be also applied for the hyperthermia of the brain tumors in alternating magnetic field that might be further enhanced with radio- or radioimmunotherapy43,44. Thus as was shown in phase III trials combination of radiotherapy and hyperthermia in comparison to the radiotherapy alone proved to be beneficial in terms of local control and survival45,46.
The obtained results suggest that MSNs are suitable for penetrating the blood-brain barrier of tumors.
For the synthesis of mesoporous silica particles the surfactant CTABr (cetyltrimethylammonium bromide) was dissolved in a mixture of water/ethanol/ammonia and then tetraethylorthosilicate (TEOS) was added to this solution as a precursor of the silica as described earlier47,48. The reaction mixture was stirred for 2hours for aging of the silica gel. The obtained precipitate was dried in the air at 473K for 1hour and after was calcinated at temperature 873K (heating rate was 5K/min) for 40minutes.
The metal-containing MSNs derivatives were synthesized by insertion of ferric chloride (III) solution (50% from saturated concentration) in the porous of the silica. The Fe metal precursor was added to the calcinated pre-formed MSNs by vacuum impregnation at residual pressure of 0.1mm Hg followed by removing the ferric chloride excess from the surface of the silica grains by washing with methylene chloride. For the reduction of FeCl3 to Fe0 samples were put in the H2 flow at 600°C for 6hours.
The morphology of the obtained Fe(0)@MCM-41 nanoparticles was controlled by scanning electron microscopy (JEOL JEM 3010). The field-emission scanning electron microscopy (FE-SEM Hitachi SU8020) equipped with an energy disperse X-ray spectrometer was employed for element analysis. The structural properties of MSNs impregnated with zero-valent Fe were analyzed by means of Bruker D2 Phaser diffractometer (XRD) supplied with a Cu sealed tube (X-ray source; λ=0.1542nm) and a LYNXEYE detector and as well as by a standard Mössbauer spectrometer (POLON) provided with a 57Co/Rh source of γ-radiation. Magnetic properties of Fe(0)@MCM-41 nanoparticles were studied using a magnetometer (Oxford Instruments Ltd). Additionally the magnetic properties of conjugates were verified by measurements of second harmonic generation by them in parallel weak ac and steady state magnetic fields (NLR-M2).
All the cell lines: (i) rat C6 glioma; (ii) HeLa; (iii) U87; and (iv) K562 were kindly provided by the Institute of Cytology of the Russian Academy of Sciences (St. Petersburg, Russia) from the Russian Cell Culture Collection. HeLa as well as C6 cells were cultured in CO2-incubator (at 37°C in presence of 6% CO2) in DMEM supplemented by 2mM L-glutamine, 10% fetal bovine serum (FBS), and antibiotics: Streptomycin (100 units/mL) and Penicillin G (100μg/mL). U87 and K562 cells were cultured in complete RPMI-1640 cell medium augmented by 10% FBS.
Rat monocytes were isolated from whole blood using ficoll gradient centrifugation. Cells were harvested in RPMI-1640 supplemented by 2mM L-glutamine, 10% FBS as well as antibiotics: Streptomycin (100units/mL) and Penicillin G (100μg/mL).
Rats’ dermal fibroblasts were obtained from cells that migrated from rabbit skin fragments as was described earlier49. Briefly, the skin fragments were cut into small, 0.1×0.1cm pieces that were cultured in DMEM cell medium, augmented by 2mM L-glutamine, 10% fetal bovine serum (FBS) as well as antibiotics (0.1mg/ml streptomycin and 100U/ml penicillin G). In 3–4 weeks, a confluent fibroblast cell monolayer was developed on a plate surface. The cell viability was determined by 0.4% trypan blue exclusion.
For analysis of nanoparticles cytotoxicity the non-radioactive cytotoxicity assay CytoTox 96 (Promega Inc., USA) was applied in accordance with the manufacturer’s protocol. Briefly, C6 glioma, U87, HeLa cells, K562, PBMCs and fibroblasts were co-incubated during 1, 3, 12 and 24hours with MSNs or Fe(0)@MCM-41 taken at different concentrations (1, 5, 10, 50, and 150μg/ml). Then supernatants were collected and concentration of lactate dehydrogenase (LDH) in the samples was determined.
Production of ROS in tumor and normal cells was detected using a dichlorodihydrofluorescein diacetate (DCDHF) fluorescent probe (C2938) obtained from Molecular Probes. Cells were exposed to 10μM DCDHF in serum-free medium for 30min at 37°C. Then cells were washed and incubated in phenol-red-free medium with MSNs and Fe(0)@MCM-41 particles for 1, 3, 12 and 24hours. Fluorescence monitoring was fulfilled by employment of a microplate fluoremeter with wavelengths of 485 (for excitation) and 538nm (for emission).
The confocal microscopy was applied for assessment of cellular interactions of nanoparticles. C6 glioma, HeLa cells, U87, K562, PBMCs and fibroblasts (1×106 cells/ml) were permitted to settle on glass slides coated by poly-L-lysine. Cells were co-incubated for 1, 3, 12 and 24hours with MSNs or Fe-MSNs (both at 150μg/ml) in CO2-incubator at 37°C. Nuclei staining with 4,6-Diamidine-2-phenylindole solution (DAPI) (Vector Laboratories, Burlingame, CA, USA) was used for all types of cells. Fluorescence images were registered with using a Leica TCS SP8 confocal technique (Leica Microsystems, Heidelberg, Germany).
MSNs or Fe(0)@MCM-41 particles were co-incubated with cells for 24h cells at concentration of 150μg/ml. Following incubation cells were fixed for 1h at 4°C in 2.5% glutaraldehyde dissolved in 0.1M cacodylate buffer with pH 7.4. To adapt the samples for electron microscopy the cells were embedded in Epon and Araldit, and then sectioned in a LKB ultratome by a diamond knife. Utrathin sections placed on fine mesh copper or nickel grids, were finally colored with uranyl acetate and lead citrate for investigation by electron microscope (Zeiss Libra 120).
Wistar rats (male) with weight 300–320g were obtained from animal nursery “Rappolovo” RAMN (St. Petersburg, Russia). The approvement have been provided by the local ethical committee of I.P. Pavlov State Medical University (St. Petersburg, Russia) for all experiments with animals in accordance with institutional guidelines for the welfare of animals.
Rodents were anesthetized intraperitoneally with 0.2ml 2% Rometar (Bioveta, Czech Republic) and 10mg “Zoletyl-100” (Vibrac sante Animale, France) before they were positioned into the stereotactic frame (David Kopf Instruments, Tujunda, CA). C6 glioblastoma cells (5×106cells/ml) in 15μl were used for injection into the nucl.caudatus dexter.
On the 15thday after inoculation for comparative analysis of the magnetic nanoparticles retention in the tumor, rodents were randomly divided into four groups (6 animals each) with purpose of: (1) the phosphate-buffer solution (PBS) injection by i.v. (control group); (2) i.v. injection of MCM-41; (3) i.v. injection of the Fe(0)@MCM-41 (2.5mg/kg) for 24hours; (4) i.v. injection of Fe(0)@MCM-41 (10mg/kg) for 24hours. Brain tumors were imaged using high-field (11.0T) MRI scanner (Bruker). T2-weighted images (TR 4200ms; TE 36ms and Flip angle 180°) were obtained in coronal plane with slice thikness 1.0mm. Additionally we performed T1-weighted images (TR 1500ms; TE 7.5ms and Flip angle 180°) as well as gradient echo images (TR 350ms; TE 5.4ms and Flip angle 40°) in coronal planes. Retention of the Fe(0)@MCM-41 particles in the glioma was assessed using multi-slice multi-echo (MSME) sequences. Analysis of images was carried out with application of software Analyze (AnalyzeDirect, Inc., Overland Park, KS). For estimation of a change of contrast on the T2 maps the calculations of T2 values were fulfilled with the help of software package Paravision 3.1 (Bruker BioSpin GmbH, Rheinstetten, Germany).
Animals were sacrificed using 150–200mg/kg of pentobarbital (administered intra-peritonealy) and then perfused with 100ml of saline and 4% paraformaldehyde for histological analysis. The whole brains were collected and fixed in 4% paraformaldehyde and 30% sucrose. The embedded in Tissue-Tek compound blocks were cut into serial 5–7μm sections for histology. Sections were treated additionally by DAPI. Fluorescence data were acquired by confocal technique Leica TCS SP8 (Leica Microsystems, Heidelberg, Germany). Reflecting laser scanning with laser exciting at 488nm (Ar/Kr) was applied for detection of Fe(0)@MCM-41 particles.
Measurements of nonlinear longitudinal response (NLR-M2) under action of dc and ac magnetic fields with parallel orientation, H+h·sin(2πft) (h=13.8Oe, f=15.7MHz), were applied for analysis of the brain tumor targeting efficiency by mesoporous silica nanoparticles and biodsitribition assessment. The symmetric relative to the point H=0 and periodic with frequency Fsc=8Hz scanning of dc field H was employed in all the experiments except of experiment in vitro with solution of Fe(0)@MCM-41 NPs (similar to that used for injections), where the value of Fsc was changed in the range 8÷10−2Hz to clarify the magnetic state of NPs. The symmetrical H-scan was convenient for observation of signal field hysteresis.
In 24hours after intravenous infusion of nanoparticles (or PBS in control group) rodents were sacrificed and tissue’s probes (mass of every one being approximately 100mg) were taken from organs and tumor (3 samples from each organ and glioma) for magnetic measurements. There were probes from heart, spleen, kidney, lungs, liver, skin, muscle as well as from normal brain and glioma. Both phase components ReM2 and ImM2 of second harmonic of nonlinear response were registered as function of steady field H. The nonlinearity of response was provided by a presence of magnetic nanoparticles in samples under study, their signal being recorded against a background signal of molecules in possible paramagnetic state in tissues50. Adapted for studying of magnetic nanoparticles, described earlier, home-made installation was employed in this study51,52. The integral sensitivity of M2- measurements was 10−10emu52.
The one-way analysis by Kruskal-Wallis was applied for detection of the differences. Comparisons of data for the groups of rodents under study were assessed using Student’s t-test. The software program used for the statistical analysis was Statistica Version 9.2. In all experiments, distinctions were regarded as statistically reliable at P<0.0553.
How to cite this article: Shevtsov, M. A. et al. Zero-valent Fe confined mesoporous silica nanocarriers (Fe(0)@MCM-41) for targeting experimental orthotopic glioma in rats. Sci. Rep. 6, 29247; doi: 10.1038/srep29247 (2016).
The authors are grateful to Nan-Jong Lee for designing of Figure 6; Olga G. Genbach for help in experiments in vivo on rodents; Marina M. Martynova and Olga A. Bystrova for electron microscopy studies; Anastasiya L. Mikhrina for histological assay; Anatolii V. Dobrodumov for magnetic resonance imaging and Boris P. Nikolaev for discussions on the NMR studies. The study was supported by the Russian Foundation for Basic Research 15-08-08148A, megagrant No. 14.B25.31.0017 of the Russian Ministry of Science and Education; investigation of animals were partly supported by a grant of the Russian Science Foundation 14-50-00068 and by the Federal Agency of Scientific Organizations, Russia, State Grant of the Ministry of Health of the Russian Federation No. 32, and by a DFG grant SFB824/2, Germany.