Ultrasensitive photodetectors exploiting electrostatic trapping and percolation transport

Abstract

The sensitivity of semiconductor photodetectors is limited by photocarrier recombination during the carrier transport process. We developed a new photoactive material that reduces recombination by physically separating hole and electron charge carriers. This material has a specific detectivity (the ability to detect small signals) of 5 × 1017 Jones, the highest reported in visible and infrared detectors at room temperature, and 4–5 orders of magnitude higher than that of commercial single-crystal silicon detectors. The material was fabricated by sintering chloride-capped CdTe nanocrystals into polycrystalline films, where Cl selectively segregates into grain boundaries acting as n-type dopants. Photogenerated electrons concentrate in and percolate along the grain boundaries—a network of energy valleys, while holes are confined in the grain interiors. This electrostatic field-assisted carrier separation and percolation mechanism enables an unprecedented photoconductive gain of 1010 e per photon, and allows for effective control of the device response speed by active carrier quenching.

Photodetectors, devices that convert photons to electricity, are widely used in digital imaging, optical communications, remote sensing, night-time surveillance, medical imaging and so on.1,2,3 Their sensitivity, the ability to differentiate signal from noise, is key for high-fidelity photon detection and imaging, especially when the signal is weak. To achieve superior sensitivity, a high gain is crucial to amplify the signal far above the noise baseline. One way to accomplish this is to multiply the photogenerated charge carriers in a single carrier transport and collection cycle, as done in photomultiplier and avalanche photodiode devices, which achieve typical gains of 103–108 carriers per incident photon4,5. However, the required high bias (hundreds to thousands of volts) and their bulky nature restrict their integration with micro-electronics for digital imaging. In addition, the electron multiplication processes give rise to excess noise. The other approach towards high gain is to collect each photocarrier multiple times over many transport cycles in simple, two-terminal devices with semiconductor channels3,6,7,8. These devices, known as photoconductors (a subset of photodetectors), are designed to trap the minority charge carriers for a long time, enabling majority carriers to recirculate through the device many times before recombining. In this way, multiple carrier collection occurs with the absorption of one photon. Small and simple in design, photoconductors are compatible with modern micro-electronics, and can be integrated as, for example, pixel sensors in the widely used CMOS (complementary metal–oxide–semiconductor) technologies.

The performance of a photoconductor device depends critically on the deliberate control of minority carrier trapping with the goal of achieving long carrier lifetime while preserving the high-mobility, low-noise majority carrier transport. Typically, minority carriers are retained in sub-bandgap states or electrostatic barriers induced by defects, dopants, electronic junctions or a combination of these factors1,6,7,8,9. However, these minority carrier traps are often in the pathway of majority carrier transport, leading to carrier scattering, reduced mobility and noise, which limit the photon sensitivity.

Here we present a novel strategy to engineer a heterogeneous system with unprecedented photo-sensitivity by sequestering the majority and minority carriers in different local domains using grain boundary delta doping (GBDD). We take advantage of the discovery by Cahen and co-workers10,11 that chloride doping at grain boundaries (GBs) in CdTe polycrystalline films establishes local p–n junctions that localize electrons in the GB regions, and direct holes towards the grain interiors (GIs). We engineer the GB doping, density and connectivity by exploiting the versatile surface chemistry of colloidal nanocrystals (NCs), and fabricate a photoactive film via kinetically controlled sintering of Cl-capped CdTe NCs. The spatial separation between photogenerated electrons and holes and the defect passivation in the GBs enables low-noise electron transport and high photoconductive gain simultaneously. We further demonstrated that electrostatic quenching enables a device reset in about 100 μs, much faster than previously reported high-gain photoconductors8,9.

Results

Materials design and properties

In the last decade, there have been significant advances in surface modification of colloidal NCs12,13,14. Here we propose the new concept of GBDD to take advantage of the rich surface chemistry of NCs for bottom–up fabrication of mesoscale materials. We prepared CdTe NCs surface modified with the eventual dopant atoms, in this case Cl. We controllably annealed arrays of NCs so that they sintered into polycrystalline films, during which process Cl selectively segregates to the GBs, doping these regions n-type (Fig. 1, Supplementary Fig. 1). The engineered GBDD establish built-in electric fields making the GIs fully depleted. These fields guide hole trapping in GIs and facilitate electron percolation along the GBs (Fig. 2).

Figure 1
Materials design and fabrication.
Figure 2
Materials properties and device design.

The spatial heterogeneity in doping, electrostatic potential and electronic transport—critical to the designed photodetector—are characterized by local microscopy and spectroscopy techniques. Nano-Auger electron spectroscopy confirmed that Cl is concentrated in the GBs of the sintered polycrystalline film (Supplementary Fig. 2). Local potential variations are resolved by Kelvin probe force microscopy (KPFM)15,16, revealing that the Fermi level of GBs and GIs are about −4.4–4.5 eV and −4.8–4.9 eV (relative to vacuum level), respectively (Fig. 2a–c and Supplementary Fig. 3). Since the conduction band minimum (CBM) and valence band maximum (VBM) are at approximately −4.3 eV and −5.8 eV, respectively (relative to vacuum level)17, we conclude that the GBs are heavily n-doped while the GIs are weakly n-doped or nearly intrinsic (Fig. 2d). Spatial current mapping using conductive atomic force microscopy (CAFM) revealed a higher conductivity in GBs compared with GIs (Supplementary Fig. 4), as expected from the higher carrier concentration and trap-passivation in the GBs. Note that a previous work showed the process of sintering Cl-capped CdSe NCs into a high-mobility film, but neither the spatial distribution of Cl nor its role in doping was identified or discussed14.

Our film properties contrast with those of the traditional top–down deposited CdTe polycrystalline films, which have micron scale grains10,11 significantly larger than those in our films (50–200 nm). The potential in these large grains is mostly flat with small band bending only near the GBs (about 100 mV), due to the less effective Cl doping in GBs and the small depletion region width (about 200 nm). Although used for efficient solar cells, these films are not applicable for high-gain photoconductors since photocarriers in the flat band and low-barrier GB regions are subject to rapid recombination. This is due to a lack of driving field for carrier separation in the GIs and the overlap of the transport pathways of electrons and holes (holes can tunnel through GBs), which yield short carrier lifetimes (nanoseconds to microseconds)18,19.

Our bottom–up fabricated device has several advantages compared with previous high-gain detectors: long carrier lifetime up to about 10 s, due to the long spatial separation between electrons and holes (tens of nm) and the large electrostatic potential barriers (hundreds of mV) between them; low-noise electron transport with high mobility, achieved by GBDD and trap-passivation in the GBs; tunable response time since the hole trapping electrostatic barrier can be overcome by pulsed injection of electrons leading to rapid recombination; low-cost solution-processable and scalable fabrication process, where the thickness of the film can be tuned by changing the concentration of the NC solutions and/or by repeating the spin-coating and annealing procedures multiple times.

Electronic transport

Field-effect transistor (FET) measurements under dark conditions confirmed n-type electronic transport (Fig. 3). Since the GBs form a network with a large electrostatic electron confinement energy (around 0.4 eV with no or small gate bias) and a higher conductivity than the GIs, we expect the GBs to be the dominant electron transport pathways. From the gate bias-dependent current, we obtain a spatially averaged field-effect mobility of μFET~5.2±2.3 cm2 V−1 s−1 and a conductivity of σ~10−4–5 × 10−3 S cm−1 at VG=0 V from devices made from several batches of CdTe NCs, with the best μFET~10 cm2 V−1 s−1. The actual mobility and conductivity of the GBs can be much larger since most of the volume of the material is occupied by the GIs, which are inactive for transport in the dark. Quantitative carrier concentration analysis from the KPFM and FET results further confirms that electron transport occurs mainly through GB regions (Supplementary Note 1).

Figure 3
Electronic transport.

We performed control studies of films sintered from CdTe NCs with no Cl or with traditional top–down Cl treatments (Supplementary Note 2), and found that they have inferior structure and much lower mobility (Supplementary Figs 5 and 6). This is strong evidence that Cl is an essential ingredient for a high-mobility film and that our bottom–up GBDD approach (incorporating Cl onto the NC surface before sintering) is key for efficient Cl doping.

Photoconduction

To explore the photo-sensitivity of the material, we fabricated photoconductor devices based on 300–400 nm thick CdTe films (Fig. 4a). Figure 4 reports the photoresponse of two representative devices with channel widths of 2 mm and 80 μm and the same length of 5 μm. Photocurrent was generated by shining collimated, monochromatic light onto the entire channel region of the device. Our devices have a large dynamic range, sensitive to light intensities varying over 9 orders of magnitude (Fig. 4b–d, Supplementary Fig. 7). The photoconductive gain and responsivity (photocurrent divided by incident photon power) increases with the decrease of photon intensity until the power reaches 5 × 10−9 mW cm−2. This is a typical behaviour for high-gain photoconductors due to the dispersion in the activation energies of the carrier trapping sites8,9. When the power is below 5 × 10−9 mW cm−2, the external photoconductive gain (the number of collected photocarriers per incident photon) saturates at Gext≈1 × 1010 and the responsivity reaches R≈4 × 109 A W−1 (at the wavelength of 500 nm). Both values are independent of the channel width and are the highest among all the visible and infrared photoconductors known in literature. We found that the film absorbs about 65% of the incoming light, and thus the internal gain (the number of collected carriers per absorbed photon) is also of the order of 1010. To understand the gain mechanism, we can approximate the internal gain as Gint=τlifetime/τtransit˙ηsep, where τlifetime is the minority carrier lifetime, τtransit is the transit time of the majority carrier (time to move form source to drain), and ηsep is the charge separation efficiency (the efficiency of carrier separation after photogeneration of electron–hole pairs, which we assume to be close to unity due to the strong built-in electric fields)2. From this equation, we can see that the gain will increase with decreasing channel length (thus shorter transit time) up until the grain size limit.

Figure 4
Photoconduction.

These photodetectors are responsive to photons with wavelength <850 nm, the bandgap of bulk CdTe, covering the entire visible and a small part of near-infrared spectrum (Fig. 4e). The responsivity is nearly constant over the range of 400–800 nm, a property highly desirable for visible camera applications.

Noise analysis

To determine the sensitivity of the device, we measured the dark noise current (Inoise) and calculated the noise equivalent power (NEP), which represents the minimum detectable power at which the signal-to-noise ratio (SNR) is unity (Fig. 5) (see Methods for details on noise measurements). We found that the noise current at 0.1 Hz (the intrinsic bandwidth of the detector, inverse of the carrier lifetime, as shown later) is more than 1 order of magnitude larger than the shot noise limit, given by An external file that holds a picture, illustration, etc.
Object name is ncomms11924-m1.jpg, where e is the elementary charge. The frequency dependence of the noise reveals that the 1/f noise (also called flicker noise, characterized by the relation Inoise2[proportional, variant]1/fα, where α is close to 1) dominates at low frequencies (f<10 Hz in this case), while at higher frequencies the noise current approaches the shot noise limit. This low-frequency noise has been widely observed in almost all known electronic devices20,21. Its exact mechanism is still not fully understood but it has been shown that more carrier-scattering defect sites induce higher levels of 1/f noise20,21,22. Compared with previously reported noise measurements on cadmium chalcogenide NC films and polycyrstalline films, our devices show a much less 1/f noise22,23, with a 1/f noise to shot noise ratio of about 2 orders of magnitude smaller (for f<10 Hz).

Figure 5
Noise and sensitivity analysis.

We calculated the bandwidth-normalized NEP using the equation NEP=Inoise/R, where R is the responsivity, and Inoise was measured at a frequency of 0.1 Hz. As discussed later, we can take R=3 × 109 A W−1 at 0.1 Hz and 10 V bias. This gives an NEP of 2.3 × 10−20 Hz−1/2 and 3.3 × 10−21 W Hz−1/2 for the devices with 2 mm and 80 μm channel width, respectively. Using a bandwidth of B=0.1 Hz, the NEP corresponds to 1 photon per 55 s (7.3 × 10−21 W) and 1 photon per 360 s (1.1 × 10−21 W), respectively, for a wavelength of 500 nm. We expect even lower NEP for smaller devices. This is an extremely high sensitivity compared with other high-performance detectors, such as PbS quantum dot photodetectors6, graphene-quantum dot hybrid photodetectors8 and commercial single-photon counting modules (SPCM) made from Si avalanche photodiodes (Fig. 5c) (see Methods for SPCM models). In cases where the photon flux is <1 photon per second, device operation speed is not a limiting factor and our detector has significant advantage over others in accurate photon sensing. However, it should be noted that lower NEP does not necessarily mean a higher SNR at all the photon power ranges. Under strong light, our device has a lower responsivity and thus may have lower SNR than photodiode-based devices.

The ultralow noise level can be attributed to the unique electronic properties of GBs and the percolation transport mechanism. It has been shown that Cl in the GBs of CdTe pushes the sub-bandgap defect states towards the VBM while moving the Fermi level close to the CBM24. Since the GBs in our device are heavily doped with Cl, we expect the sub-bandgap states to be filled lying far below the Fermi level and thus do not contribute to carrier trapping and scattering. This leads to a strong suppression of the 1/f noise that typically dominates disordered semiconductors at low frequencies (f<1 kHz)21,22. Another common source of noise that occurs in photodetectors under illumination is generation–recombination (g–r) noise, which originates from photocarrier trapping and detrapping processes25. We also expect the g–r noise to be small in our detector due to the long spatial separation between electrons and holes and the high-mobility GBs pathways for electron conduction. This is in sharp contrast with traditional polycrystalline films where the majority carriers are generated and transported through GI regions and are scattered at GBs which possess different chemical potentials than the GIs10,11.

Temporal response

Besides the gain and noise level, a photodetector's temporal response also determines the extent of its applications. As previously explained, high gain in photoconductors requires long carrier lifetime, and as a result these detectors typically have slow response, in the scale of 10−2–104 s (refs 8, 9). Figure 6a shows the time-resolved photocurrents of our photoconductor under two different light intensities. At high intensity, the photocurrent decay consists of two components: a fast decay on the scale of 1 ms, and a slow decay of ~10 s. At lower intensity, the slow component dominates. The rise time for both power levels is in the scale of 1 ms. In the low-light case, we can see that the photocurrent decayed to ~20% of the on-state value after the light was switched off for about 10 s (similar results were obtained for even lower photon flux). Therefore we expect the responsivity at the low-light limit to be ~3 × 109 A W−1 (80% of the direct current direct current (DC) value) under an AC modulation of 0.1 Hz (with a few ms on-time and 10 s off-time). We can also estimate that τlifetime≈10 s. Taking Gint≈1010 and assuming that ηsep=1, we calculated τtransit≈1 ns, which corresponds to a mobility of ~60 cm2 V−1 s−1 (Supplementary Note 4). This mobility is an order of magnitude higher than the measured bulk FET mobility, likely due to the volume averaging effect of the latter value, as mentioned above. Therefore, we expect that the actual mobility in the GBs to be in the scale of several 10 s of cm2 V−1 s−1. Note that in cases where ηsep<1, we would expect an even higher mobility.

Figure 6
Temporal response.

One strategy to improve the device response speed in high-gain detectors is to apply a gate voltage pulse8,26. Reset or quenching circuits are also widely used in photomultipliers and avalanche photodiodes. Since the hole traps in our device are electrostatic in nature, we expected that a positive gate pulse would flood the channel with electrons causing partial band flattening between the GIs and GBs, which reduces the electrostatic barrier yielding efficient electron–hole recombination (Supplementary Note 5). We employed this mechanism in a photo-FET (the same device structure as shown in Fig. 3a) and implemented a reset protocol: a 5 V gate pulse applied for 1 ms (Fig. 6b,c, Supplementary Fig. 10). The source current rapidly decreased and changed sign within 1 μs (switch time of the light), and gradually returned to the original dark current value within about 100 μs. This sign switch reveals that the source–drain transport current (electrons injected from the source to the channel and collected by the drain) decayed within 1 μs after the gate was switched off, and the injected electrons left the channel via the source and drain electrodes within 100 μs. Therefore, when the gate pulse was applied, the photocurrent decay mechanism changed from slow hole decay to fast electron decay, increasing the speed by 5 orders of magnitude. The absence of the sluggish minority carrier decay current confirms our proposed mechanism of electron–hole recombination on application of the gate pulse and is consistent with the proposed electrostatic trapping scheme (Fig. 6d). Note that this strategy is not as efficient in photoconductor devices that employ (or partially employ) sub-bandgap trap states which require higher pulse voltages to obtain only a modest improvement in response speed8,9.

Discussion

Specific detectivity D* is a standard measure of the detector sensitivity that represents the intrinsic materials properties, independent of the device geometry1,2. We can calculate the specific detectivity An external file that holds a picture, illustration, etc.
Object name is ncomms11924-m2.jpg from the measured NEP and the device area A. In our devices, D*≈5 × 1017 Jones (cm Hz1/2 W−1), the highest reported for all the visible and infrared photodetectors operating at room temperature. In comparison, the specific detectivity of single-crystal silicon photodiodes is about 1 × 1013 Jones (ref. 27), and that of the graphene-quantum dot hybrid photodetector (one of the most sensitive photoconductor devices) is 7 × 1013 Jones (ref. 8).

This solution-processed, scalable detector with remarkable sensitivity and rapid response enabled by GBDD is compatible with both video-rate pixelated imaging and large-area photon detection, and should excel in applications where the detection of low levels of photons is demanded (Supplementary Notes 6 and 7). There are many situations where the photon source is naturally weak. For example, at night time the trace amounts of light from moon, star or other celestial objects can be close to or lower than 1 photon per second. Our detector, with extremely low NEP, may have advantage in this case for colour night vision28. There are other situations where reducing the photon exposure is highly desirable, for example, in medical X-ray detectors where X-ray generates electron–hole pairs in semiconductors and create electrical signals29. The much higher detectivity in our polycrystalline CdTe device compared with single-crystalline counterparts could enable significant reduction of X-ray dosage, promising for diminishing negative radiation effects on the human body during the X-ray imaging.

The GB doping and conduction properties are not unique to the CdTe system. In fact, GB-assisted photocarrier collection has been reported in a wide variety of emerging photovoltaic materials, such as Cu(In, Ga)Se2 (CIGS), Cu2ZnSnS4 (CZTS) and organic–inorganic halide perovskites30,31,32,33. Similar to CdTe polycrystalline films, these materials are currently fabricated mostly via top–down approaches. We expect that the bottom–up GBDD approach demonstrated here would be applicable in these systems as well. By tuning the surface chemistry of the NC building blocks and the sintering conditions, we can spatially organize the grain size, GB doping and connectivity, therefore modulating the charge transport, photoconduction and/or photovoltaic properties.

The demonstrated concept of mesoscale percolation pathway engineering can have potential impacts in other electron-based materials and devices beyond optoelectronics, involving the interaction of electrons with other degrees of freedom such as spin and phonons. As an example, in thermoelectrics we can envision a heterogeneous system where electronic transport and thermal transport take place via different pathways, and thus high electrical conductivity and low thermal conductivity can be achieved simultaneously, enhancing the thermoelectric figure of merit34.

Methods

NC synthesis

CdTe NCs capped with cadmium oleate (Cd(Oleate)2) with sizes of ~5 nm were synthesized by hot injection following a procedure modified from one previously reported35. Specifically, 4.8 g CdO, 42 g oleic acid and 40 g octadecene were combined in a 500 ml three-neck round bottom flask. This mixture was degassed under vacuum at 100 °C for an hour. Meanwhile, two identical solutions of Te in tributylphosphine (TBP) were prepared: 1.5 g Te and 12 ml TBP were added to a 24-ml vial and heated to 220 °C until the powder dissolved and the solution became clear and yellow (in about 90 mins). Once a clear yellow solution was reached, it was cooled to room temperature. After degassing the contents of the flask, the head space was backfilled with argon and heated to 270 °C to form the cadmium oleate complex indicated by a colour change from red to clear and colourless. Once the temperature stabilized at 270 °C, the flask was quickly removed from the heating mantle and the Te/TBP solutions were swiftly and simultaneously injected through 16 gauge needles into the hot solution. On injection, the clear solution quickly changed to a dark colour. The flask was quickly cooled to room temperature by spraying air and isopropanol from a wash bottle on the flask. After the solution cooled, the flask was connected to a distillation apparatus and the volatiles were vacuum distilled at 130 °C and 55 mtorr until ~40 ml of liquid remained. The crude product in the still pot was transferred via cannula to a Schlenk flask and stored in an argon-filled glovebox.

NC purification

NCs were isolated and purified in an argon atmosphere. Approximately 10 ml of the crude product was added to a 50 ml centrifuge tube, filled with methyl acetate to 40 ml total volume and then centrifuged at 8,000 r.p.m. for 5 min. The clear supernatant was disposed and the formed dark coloured pellet with small amount of white content was dispersed in a small amount (3–4 ml) of pentane. Methyl acetate was added to a total volume of 50 ml creating a turbid solution which was centrifuged at 8,000 r.p.m. for 5 min. The nearly clear supernatant was disposed and the pellet was cleaned with three additional pentane/methyl acetate washing steps. By the last step, the pellet no longer contained a white residue. Finally, the pellet was dispersed in 20 ml of toluene and filtered into a clean glass vial with a 0.2 μm PTFE syringe filter. The solution was then dried under vacuum until all volatiles were removed. The dried residue was dispersed in toluene reaching a concentration of 1.5 mM determined from optical absorbance36.

NC surface modification with chloride

CdTe NCs surface reaction was performed in an argon environment by adopting protocols established for CdSe-Cd(oleate)2 NCs13,14. It is crucial to remove the residual water from all reagents and solvents using rigorous drying methods. To begin, 4 μmol CdTe-Cd(oleate)2 NCs (2.7 ml of 1.5 mM NC solution) was added to a glass vial. TBP was added to the NC solution to a concentration of 500 mM. While the solution was stirred, 1.4 ml of trimethylsilychloride (TMSCl) was added (12 TMSCl molecules per nm2 of NC surface). After the solution was stirred for 1 h, the volatiles were removed by vacuum distillation at room temperature (a small amount of liquid remained, presumably the TBP). After distilling for 1 h, 3 ml of toluene was added to the remaining product and the vial was shaken to facilitate uniform mixing and then centrifuged at 4,000 r.p.m. for 5 min. The clear supernatant was disposed and 5 ml of toluene was added to pellet and stirred. About 147 μl octylamine (three molecules per nm2 of NC surface) was added and the NCs immediately dispersed. After stirring for 1 h, methyl acetate was added to flocculate the solution, which was then centrifuged at 4,000 r.p.m. for 5 min. The supernatant was then disposed. The toluene/octylamine/methyl acetate step was repeated two more times. The final pellet was dispersed in 5 ml toluene, filtered with a 0.2 μm PFTE syringe filter into a clean glass vial, and then dried under vacuum for 1 h. The dark residue was dispersed in toluene to a desired NC concentration.

Film and device fabrication

Nanostructured CdTe polycrystalline films were formed by sintering spin-coated CdTe NC solution in an inert environment. 300 nm SiO2/n Si or quartz substrates were cleaned by subsequent sonication in acetone and isopropanol, then dried with filtered nitrogen and finally exposed to oxygen plasma. A drop of CdTe NC in toluene solution (typically around 0.5 mM) was deposited on the substrate and spin coated at 1,500 r.p.m. The substrate was then placed on a hotplate held at 350 °C for 30 s to 5 min, yielding a polycrystalline film with thickness of about 50–100 nm. In cases where thicker films were desired, the spin-coating and annealing procedures were repeated multiple times (layer-by-layer deposition). Thick films can also be fabricated using higher NC concentrations. FET and photoconductor devices were fabricated by thermal evaporation (using shadow masks) of 60 nm indium and 40 nm gold on the CdTe polycrystalline film deposited on SiO2/Si and quartz substrates, respectively. Channel length and width are determined by optical microscopy and/or atomic force microscopy on the final devices.

Local microscopy and spectroscopy characterization of the sintered film

CdTe films were prepared on n Si substrates (with native oxide) for local imaging and spectroscopy measurements.

Zeiss Gemini Ultra-55 scanning electron microscope (SEM) was used to image the top–view and cross-section morphology of the fabricated one layer and multiple layer films. Energy-dispersive X-ray spectroscopy was performed during SEM imaging which also confirmed the existence of Cl in the CdTe film.

Nano-Auger electron spectroscopy was performed on one layer CdTe films using an Omicron system equipped with a field emission gun as an electron source. The vacuum level was 10−10 mbar, and the spatial resolution was ~10 nm limited by the diameter of the focused electron beam.

Conductive AFM (CAFM) and KPFM were performed on one layer CdTe films using an Agilent AFM (with home-built feedback loop for the KPFM) in an inert atmosphere. Cr/Pt-coated tips with a spring constant of ~0.2 N m−1 (from BudgetSensors) were used for CAFM, while Ti/Pt-coated tips with a spring constant of ~2 N m−1 and a resonance frequency of ~70 kHz (from Olympus) were used for KPFM. Surface potential was calibrated by setting that of the grounded Au film to −5.1 V (taking its work function to be 5.1 eV)16.

Transport and photoconduction measurements

All measurements were performed under inert atmosphere. DC I–V curves were measured using a Keithley 2636a dual source-meter. For photocurrent measurements, a xenon lamp combined with a monochromator was used to generate monochromatic visible/near-infrared light, which was collimated and directed towards the sample. Light intensity was controlled by neutral density filters and measured using a commercial Si photodiode (FDS1010 from Thorlabs). Photocurrent was determined from the DC current under illumination after subtracting the dark DC current. Spectral responsivity measurements (Fig. 4e) were performed under a modulation of 75 Hz for different photon wavelengths.

Time-resolved photocurrent measurements (Fig. 6) were performed by generating light pulses from an LED (M660L3 from Thorlabs) using an Arduino electronics board. Short-time transient current (microseconds to milliseconds) was measured with a Femto low-noise current amplifier (DLPCA-200) and a digital oscilloscope (TDS 640 from Tektronix), while long-time current traces (milliseconds to tens of seconds) were measured using the Keithley source-meters. Gate pulses were generated and synchronized with the light pulses using the Arduino board.

Noise measurements

Dark noise current (Inoise) was measured using an SR830 lock-in amplifier from Stanford Research Systems, following a previously reported procedure6. An isolated DC voltage source (SIM928 from Stanford Research Systems) was used to bias the device, and a Femto low-noise current amplifier (DLPCA-200) was used to amplify the current. The output of the amplifier was directly connected to the signal input of the lock-in amplifier for noise measurements, where the internal reference frequency was manually adjusted to the desired values. The measured Inoise is given in units of A Hz−1/2.

To validate the accuracy of the NEP measurement technique, we performed the same measurement on the FDS1010 Si photodiode. At 5 V reverse bias, we obtained a dark current of 3.6 nA and a noise current of 5.6 × 10−13 A Hz−1/2 (with a lock-in frequency of 500 Hz). The typical dark current and noise from the manufacturer's specification are 1.05 nA and 1.5 × 10−13 A Hz−1/2, close to the values we measured. Therefore we believe the measured noise current and NEP for the CdTe detectors are also accurate.

Commercial SPCMs for NEP comparison

Single-photon counters from Thorlabs with model number: SPCM20A, SPCM50A (magenta diamonds in Fig. 5c); COUNT BLUE series SPCM from Laser Components, module: COUNT-10B (blue diamond in Fig. 5c).

Data availability

The data that support the findings of this study are available from the corresponding authors upon request.

Additional information

How to cite this article: Zhang, Y. et al. Ultrasensitive photodetectors exploiting electrostatic trapping and percolation transport. Nat. Commun. 7:11924 doi: 10.1038/ncomms11924 (2016).

Supplementary Material

Supplementary Information:

Supplementary Figures 1-10, Supplementary Notes 1-7 and Supplementary References

Peer review file:

Acknowledgments

We thank Peter Denes and Jianbo Gao for discussion on photodetectors. Device fabrication and measurement was supported by the ‘Self-Assembly of Organic/Inorganic Nanocomposite Materials' program, Office of Science, the Office of Basic Energy Sciences (BES), Materials Sciences and Engineering (MSE) Division of the US Department of Energy (DOE) under Contract No. DE-AC02-05CH11231 (Y.Z., N.D.B. and M.S.). Nanocrystal synthesis and thin film preparation was supported by the ‘Physical Chemistry of Inorganic Nanostructures' program by the Director, Office of Science, Office of Basic Energy Sciences, of the United States Department of Energy under Contract DE-AC02-05CH11232 (D.J.H and A.P.A). It used resources of the Molecular Foundry, supported by the Office of Science of the US Department of Energy.

Footnotes

Patent applications may be affected by the paper.

Author contributions Y.Z., D.J.H. and A.P.A. designed the experiments. D.J.H. performed nanocrystal synthesis and sintering with the assistance of Y.Z. Y.Z., D.J.H., C.K. and D.F.O. contributed to sample characterization. Y.Z. designed and fabricated devices and performed measurements, with the assistance of N.D.B. and D.J.H. M.S. and A.P.A. supervised the project. Y.Z., D.J.H., M.S. and A.P.A analysed the results and prepared the manuscript. All authors contributed to discussions and revision of the manuscript.

References

  • Konstantatos G. & Sargent E. H. Nanostructured materials for photon detection. Nat. Nanotechnol. 5, 391–400 (2010). [PubMed]
  • Koppens F. H. L. et al. . Photodetectors based on graphene, other two-dimensional materials and hybrid systems. Nat. Nanotechnol. 9, 780–793 (2014). [PubMed]
  • Sukhovatkin V., Hinds S., Brzozowski L. & Sargent E. H. Colloidal quantum-dot photodetectors exploiting multiexciton generation. Science 324, 1542–1544 (2009). [PubMed]
  • Yamazaki I., Tamai N., Kume H., Tsuchiya H. & Oba K. Microchannel-plate photomultiplier applicability to the time-correlated photon-counting method. Rev. Sci. Instrum. 56, 1187–1194 (1985).
  • Levine B. F. & Bethea C. G. Single photon detection at 1.3 μm using a gated avalanche photodiode. Appl. Phys. Lett. 44, 553–555 (1984).
  • Konstantatos G. et al. . Ultrasensitive solution-cast quantum dot photodetectors. Nature 442, 180–183 (2006). [PubMed]
  • Lee J.-S., Kovalenko M. V., Huang J., Chung D. S. & Talapin D. V. Band-like transport, high electron mobility and high photoconductivity in all-inorganic nanocrystal arrays. Nat. Nanotechnol. 6, 348–352 (2011). [PubMed]
  • Konstantatos G. et al. . Hybrid graphene-quantum dot phototransistors with ultrahigh gain. Nat. Nanotechnol. 7, 363–368 (2012). [PubMed]
  • Lopez-Sanchez O., Lembke D., Kayci M., Radenovic A. & Kis A. Ultrasensitive photodetectors based on monolayer MoS2. Nat. Nanotechnol. 8, 497–501 (2013). [PubMed]
  • Visoly-Fisher I., Cohen S. R. & Cahen D. Direct evidence for grain-boundary depletion in polycrystalline CdTe from nanoscale-resolved measurements. Appl. Phys. Lett. 82, 556–558 (2003).
  • Visoly-Fisher I., Cohen S. R., Ruzin A. & Cahen D. How polycrystalline devices can outperform single-crystal ones: Thin film CdTe/CdS solar cells. Adv. Mater. 16, 879–883 (2004).
  • Owen J. S., Park J., Trudeau P.-E. & Alivisatos A. P. Reaction chemistry and ligand exchange at cadmium-selenide nanocrystal surfaces. J. Am. Chem. Soc. 130, 12279–12281 (2008). [PubMed]
  • Anderson N. C. & Owen J. S. Soluble, chloride-terminated CdSe nanocrystals: ligand exchange monitored by 1H and 31P NMR spectroscopy. Chem. Mater. 25, 69–76 (2013).
  • Norman Z. M., Anderson N. C. & Owen J. S. Electrical transport and grain growth in solution-cast, chloride-terminated cadmium selenide nanocrystal thin films. ACS Nano 8, 7513–7521 (2014). [PMC free article] [PubMed]
  • Zhang Y., Ziegler D. & Salmeron M. Charge trapping states at the SiO2–oligothiophene monolayer interface in field effect transistors studied by Kelvin probe force microscopy. ACS Nano 7, 8258–8265 (2013). [PubMed]
  • Zhang Y. et al. . Charge percolation pathways guided by defects in quantum dot solids. Nano Lett. 15, 3249–3253 (2015). [PubMed]
  • Khosroabadi S. & Keshmiri S. H. Design of a high efficiency ultrathin CdS/CdTe solar cell using back surface field and backside distributed Bragg reflector. Opt. Express 22, A921–A929 (2014). [PubMed]
  • Ahrenkiel R. K. et al. . Spatial uniformity of minority-carrier lifetime in polycrystalline CdTe solar cells. Appl. Phys. Lett. 64, 2879–2881 (1994).
  • Long Q., Dinca S. A., Schiff E. A., Yu M. & Theil J. Electron and hole drift mobility measurements on thin film CdTe solar cells. Appl. Phys. Lett. 105, 042106 (2014).
  • Dutta P. & Horn P. M. Low-frequency fluctuations in solids: 1/f noise. Rev. Mod. Phys. 53, 497–516 (1981).
  • Kogan S. Electronic Noise and Fluctuations in Solids 1st edn Cambridge Univ. Press (1996).
  • Lai Y. et al. . Low-frequency (1/f) noise in nanocrystal field-effect transistors. ACS Nano 8, 9664–9672 (2014). [PubMed]
  • Deen M. J., Rumyantsev S. L., Landheer D. & Xu D.-X. Low-frequency noise in cadmium-selenide thin-film transistors. Appl. Phys. Lett. 77, 2234–2236 (2000).
  • Li C. et al. . Grain-boundary-enhanced carrier collection in CdTe solar cells. Phys. Rev. Lett. 112, 156103 (2014). [PubMed]
  • Carbone A. & Mazzetti P. Grain-boundary effects on photocurrent fluctuations in polycrystalline photoconductors. Phys. Rev. B 57, 2454–2460 (1998).
  • Jeon S. et al. . Gated three-terminal device architecture to eliminate persistent photoconductivity in oxide semiconductor photosensor arrays. Nat. Mater. 11, 301–305 (2012). [PubMed]
  • Gong X. et al. . High-detectivity polymer photodetectors with spectral response from 300 nm to 1450, nm. Science 325, 1665–1667 (2009). [PubMed]
  • Waxman A. M. et al. . Progress on colour night vision: visible/IR fusion, perception and search, and low-light CCD imaging. Proc. SPIE 2736, 96–107 (1996).
  • Verger L., Bonnefoy J. P., Glasser F. & Ouvrier-Buffet P. New developments in CdTe and CdZnTe detectors for X and γ-ray applications. J. Electron. Mater. 26, 738–744 (1997).
  • Yan Y. et al. . Electrically benign behaviour of grain boundaries in polycrystalline CuInSe2 films. Phys. Rev. Lett. 99, 235504 (2007). [PubMed]
  • Li J. B., Chawla V. & Clemens B. M. Investigating the role of grain boundaries in CZTS and CZTSSe thin film solar cells with scanning probe microscopy. Adv. Mater. 24, 720–723 (2012). [PubMed]
  • Yun J. S. et al. . Benefit of grain boundaries in organic–inorganic halide planar perovskite solar cells. J. Phys. Chem. Lett. 6, 875–880 (2015). [PubMed]
  • Li J.-J. et al. . Microscopic investigation of grain boundaries in organolead halide perovskite solar cells. ACS Appl. Mater. Interfaces 7, 28518–28523 (2015). [PubMed]
  • Kim S. I. et al. . Dense dislocation arrays embedded in grain boundaries for high-performance bulk thermoelectrics. Science 348, 109–114 (2015). [PubMed]
  • Panthani M. G. et al. . High efficiency solution processed sintered CdTe nanocrystal solar cells: The role of interfaces. Nano Lett. 14, 670–675 (2014). [PubMed]
  • Kamal J. S. et al. . Size-dependent optical properties of zinc blende cadmium telluride quantum dots. J. Phys. Chem. C 116, 5049–5054 (2012).