NanoPen: Dynamic, Low-Power, and Light-Actuated Patterning of Nanoparticles


We introduce NanoPen, a novel technique for low optical power intensity, flexible, real-time reconfigurable, and large-scale light-actuated patterning of single or multiple nanoparticles such as metallic spherical nanocrystals, and one-dimensional nanostructures such as carbon nanotubes. NanoPen is capable of dynamically patterning nanoparticles over thousands of μm2 areas with light intensities <10 W/cm2 (using a commercial projector) within seconds. Various arbitrary nanoparticle patterns and arrays (including a 10×10 array covering a 0.025 mm2 area) are demonstrated using this capability. One application of NanoPen is presented through the creation of surface-enhanced Raman spectroscopy (SERS) hot-spots by patterning gold nanoparticles of 90 nm diameters with enhancement factors exceeding 107 and pico-molar concentration sensitivities.

The ability to pattern nanostructures has important applications in medical diagnosis1,2, sensing3, nano- and optoelectronic device fabrication4,5, nanostructure synthesis6, and photovoltaics7. Several techniques such as dip-pen nanolithography8-13, nanofabrication14, contact printing15-18, self-assembly19,20, and Langmuir-Blodgett21 have been used to pattern nanostructures. However, these techniques lack the capability to create real-time reconfigurable patterns without the use of complicated instrumentation or processing steps. Various optical patterning techniques22-26 have tried to overcome this challenge. Optical patterning of nanoparticles has been achieved previously by actuating an indium-tin oxide (ITO) layer as a photoconductive material and generating local current densities to concentrate the nanoparticles. However, these methods suffer from a slow patterning process22 (several minutes to hours) or they require very high optical intensities23 (~105 W/cm2) to pattern the nanostructures. These limitations prevent the widespread application of such techniques. Alternatively, optical tweezers have been used to manipulate and permanently assemble nanostructures onto the substrate24,25. Moreover, optical tweezers have been combined with local heating of nanoparticles to create convective flows for collection and patterning of particles26. However, optical tweezers are also limited to using very high optical intensities (~107 W/cm2) and high numerical aperture objectives, which limits the ease of operation, reduces the available working area, and potentially damages the nanoparticles24.

Optoelectronic tweezers (OET)27 work based on the principles of an optically-induced dielectrophoresis28 (DEP) force and have been used extensively to manipulate, separate, and organize microparticles27,29 and nanostructures30. In addition to the DEP force, two other major electrokinetic forces have been observed and studied in the OET device31, namely, light-actuated AC electroosmosis (LACE)32,33 and electrothermal (ET)34 flow. In this paper, we report the novel use of OET optofluidic platform for “directly writing” patterns of nanoparticles. We call this novel technique NanoPen. NanoPen uses various electrokinetic forces (DEP, LACE, and ET) to collect and permanently immobilize nanoparticles on the OET surface. NanoPen can be operated to collect and immobilize single and multiple nanoparticles such as spherical metallic nanocrystals and one-dimensional nanostructures such as multi-wall carbon nanotubes. We would like to note that the name NanoPen refers to a method for patterning nanoparticles (a Nanoparticle Pen) and does not mean nanoscale positioning accuracy.

Figure 1a shows the device structure for OET nanopatterning optofluidic platform. The OET device consists of a top indium-tin oxide (ITO) transparent electrode and a bottom ITO electrode on top of which there is a 1-μm layer of hydrogenated amorphous silicon (a-Si:H). The nanoparticles of interest, such as metallic nanocrystals, carbon nanotubes, and nanowires are dispersed in a KCl/DI water solution with 1-10 mS/m conductivity which is sandwiched between the top and the bottom electrode layers. There is an AC voltage applied between the two ITO electrodes, with 10-20 peak-to-peak voltage and 10-100 kHz frequency. To actuate the OET device, an optical pattern is projected on the a-Si:H layer, either by using a laser source, a spatial light modulator, or a commercial projector. The light pattern generates electron-hole pairs in the a-Si:H layer, locally increasing the conductivity of the photoconductive material, and transferring the AC voltage to the liquid layer only in the area that light pattern is present. This will create a non-uniform field distribution in the liquid layer which can interact with particles in the liquid, attracting or repelling them from areas of high electric field intensity according to the DEP principle.

Figure 1
The NanoPen mechanism. (a) Optoelectronic tweezers (OET) optofluidic platform used to realize the NanoPen process. The device consists of a bottom glass substrate covered with a 300 nm thick indium-tin-oxide (ITO) layer on top of which a 1 μm ...

In addition to the DEP force, the presence of the non-uniform electric field and the heat generated by absorption of the light pattern in the a-Si:H result in two other major electrokinetic forces. First, LACE flow32,33,35 and second, ET flow31,34. LACE flow is created due to the interaction of lateral component of electric field with the electrical double layer on the a-Si:H surface and is observed mainly at frequencies below 50 kHz. On the other hand, the absorption of the light in the a-Si:H creates a local heat gradient which in turn creates a gradient in permittivity and conductivity of the liquid layer, generating dielectrophoretic forces on the liquid layer. This force drives the liquid in a vortex flow pattern around the illuminated area; this flow is called the electrothermal (ET) flow. Figure 1b depicts finite-element simulation (using COMSOL Multiphysics) of these electrokinetic forces in the OET chamber for an applied voltage of 20Vpp at 10 kHz, with 1 mS/m liquid conductivity. The DEP28 force is modeled using FDEP=2πr3εmRe{K}E2 where r is the radius of the particle, εm is the permittivity of the media, Re{K} is the real part of the Clausius-Mossotti (C.M.), and E is the electric field; LACE flow is modeled by calculating the slip velocity36 due to the interaction of the lateral component of the electric field with the electrical double layer on a-Si:H surface, νSlip=εmξEt/η, where ζ is the zeta potential of the electrical double layer, and Et is the lateral component of the electric field; the ET flow can be modeled by calculating the temperature gradient ΔT due to joule heating in a-Si:H (σaSiE2) which results in a gradient in permittivity and conductivity of the liquid. The interaction of these gradients with the non-uniform electric field, creates a body force on the liquid given by34, <fET>=12Re[(σmεmσm+iωεm(κεκσ))(T.E)E]12E2κεεmT, where σm and εm are the liquid conductivity and permittivity, respectively, and κε and κσ are the permittivity and conductivity gradients generated due to the temperature gradient, ΔT .

The NanoPen mechanism benefits from the combination of these electrokinetic forces generated in the OET optofluidic platform. In particular, there are two distinct forces that lead to light-actuated patterning of nanoparticles: a collection force responsible for collecting the particles from long range (over 100 μm distances) and concentrating them in the light spot and an immobilization force which strongly attracts the particles (with up to 0.1 pN forces) and immobilizes them on the OET surface. The collection force benefits from DEP force attraction of particles over the short range and LACE and ET flow-based collection of the particles over the longer range. The immobilization force which is responsible for attracting the particles to the surface is mainly dominated by the DEP force but is also affected by electrophoretic forces due to the particles surface charges.

Figure 1c shows NanoPen immobilization and patterning of 90 nm diameter gold nanoparticles (purchased from Nanopartz Inc.37) dispersed in a 5 mS/m solution of KCl and DI water with ~ 1011 particles/ml concentration. In the beginning, there is no voltage applied to the device and the nanoparticles undergo Brownian motion. Once the voltage is applied (20Vpp at 50 kHz), the nanoparticles are collected in the center of the light spot (continuous-wave 633 nm diode laser, 100 μW) and are immobilized on the OET bottom surface. The stage is then manually transported leaving a trace of gold nanoparticles in the illuminated area on the OET surface. Once the immobilization process is complete, the liquid solution can be removed without damaging the patterned structure. The patterned surface remains intact after multiple rinsing and drying steps. In addition, using a diluted nanoparticle solution, NanoPen is capable of patterning single nanoparticle as depicted in Figure S1 for patterning a single 90 nm-diameter spherical gold nanoparticle. We have also demonstrated that NanoPen is capable of patterning one-dimensional nanostructures such as multi-wall carbon nanotubes (see Figure S2 in supporting information) as well as semiconducting and metallic nanowires (see Figure S3 in supporting information). The line-width and density of immobilized structures can be tuned by adjusting the AC voltage source parameters such as peak-to-peak voltage and frequency, light source parameters such as light intensity and spot size, and operational parameters such as the exposure time and light pattern scanning speed. An example of this area density tuning is shown in Figure 1d where the number of patterned nanoparticles within the illuminated area is increased by increasing the exposure time from 2 seconds to 120 seconds. After completion of the patterning process, the top ITO is removed and the remainder of the liquid is blow-dried leaving the patterned structures intact. The inset shows the SEM image of the patterned spots, the number of particles patterned ranges from ~250 particles for a 2 second exposure to ~6500 particles for a 120 second exposure (see Figure S5 in supporting information).

Since NanoPen is a light-induced patterning technique, it can be used for dynamic and flexible patterning of nanoparticles by adjusting the projected light pattern using a spatial light modulator. Moreover, the low required optical power intensity for actuation of NanoPen makes it possible to pattern the nanostructures using a commercial projector (Dell, 2400MP with 3000 ANSI Lumens, 1024x768 resolution) with <10 W/cm2 optical intensity. To demonstrate this capability, we have patterned 90 nm diameter gold nanoparticles in the form of a 10×10 array over a 150×140 μm2 area, the “NIH” logo over a 160×140 μm2 area, and the “CAL” logo over a 140×110 μm2 area, as shown in Figures 2a, 2b, and 2c, respectively. These arbitrary patterns were created through a Microsoft Powerpoint interface with the projector. The optical patterns were then focused onto the OET chip using a 20× objective. The exposure time for 10×10 spots array is 2 minutes. The slight non-uniformity in the patterns is due to the non-uniformity of the projected light patterns and could be improved through better optical alignment.

Figure 2
Large area patterning of nanoparticles using NanoPen. Patterning of 90 nm diameter gold nanoparticles in the form of (a) a 10×10 array, over 150×140 μm2, (b) “NIH” logo over 160×140 μm2,and (c) “CAL” ...

Applications of patterned nanostructures range from fabrication of opto- and nanoelectronic devices in case of nanowires and carbon nanotubes4,5 to DNA microarrays1,2 depending on the type and characteristics of the patterned nanoparticles. In recent years, metallic nanocrystals have received much attention as local, sub-diffraction limited nanosensors3 for medical and chemical diagnosis and imaging, due to their interesting plasmonic properties. Therefore, NanoPen patterned metallic nanoparticles present a method for flexible and dynamic patterning of SERS sensing structures. To explore this capability further, we tried a solution of Rhodamine 6G (R6G) dye on the surface of an arbitrary NanoPen patterned structure (Figure 3a). The NanoPen patterned SERS substrates were prepared by patterning a solution of 60-90 nm gold nanoparticles on the OET surface using the NanoPen process. Once the patterning is complete, the top ITO cover glass is removed and the remaining liquid is blow dried, leaving the patterned area intact. The two-dimensional Raman scan (at 1570 cm−1 Raman shift) of the structure indicates strong signal enhancement in the areas that nanoparticles are patterned. Moreover, we observe that positions with higher nanoparticle concentration (longer exposure time) show better enhancement relative to areas with lower particle density. A typical Raman signal achieved from R6G molecules (using a 3 mW, 532 nm laser excitation) is shown in Figure 3a inset. To quantify the SERS enhancement factor for NanoPen patterned gold nanoparticles, we dried 1-10 μL droplets of a 100 nM solution of trans-1,2-bis(4-pyridyl)ethene38 (BPE) molecules on a patterned area, followed by a two-minute rinse with methanol and water. Raman measurements were then performed using a Raman setup built around an inverted TE2000 Nikon microscope. 10×, 40×, or 60× objectives were used to focus the laser source (785 nm, 30 mW) onto the sample and collect the Raman signal. As shown in Figure 3b, the enhancement factor is calculated by comparing the Raman signal intensities acquired from the 100 nM BPE molecules dried on the SERS structures to the Raman intensities acquired from a benchmark solution of 10 mM BPE. At the 1200 cm−1 Raman shift peak, the Raman intensity for 100 nM solution for the SERS structures is 32,000 counts versus 250 counts for the 10 mM benchmark solution leading to an enhancement factor (EF) of, EF=32,000250×10mM100nM1.3×107. Figure 3b inset shows a zoomed-in version of the Raman signal of the main plot in the range 1100-1350 cm−1, with the 10 mM benchmark solution Raman signal multiplied by a factor of 25 to make it more visible. The BPE Raman signals were achieved for 4 second integration using a 30 mW, 785 nm laser source and all signal levels are measured relative to the background. In addition, we observed strong SERS signal with concentrations as small as pico-molars (see Figure S6 in supporting information).

Figure 3
Surface-enhanced Raman spectroscopy (SERS) using NanoPen patterned metallic nanoparticles. (a) Measurement of Rhodamine 6G (R6G) spectrum using the NanoPen patterned gold nanoparticle (mixture of 60 and 90 nm sizes). The 2-dimensional scan of Raman signal ...

Currently, due to the small size of the patterned particles (<100 nm), the positioning accuracy is limited predominantly by Brownian motion and the diffraction-limited spot size. Moreover, NanoPen requires the use of a photoconductive thin-film substrate for the patterning process to work. However, after patterning the structures in the desired locations, the photoconductive film can potentially be removed39 to allow further processing steps. In this work, we have focused on patterning one kind of a particle at a time. However, this limitation can be overcome through integration of NanoPen with microfluidic channels to form a complete optofluidic40 system. Such integration would help realize promising applications such as the creation of DNA microarrys. However, future investigations need to be done to study the operational conditions of NanoPen for patterning biomaterials such as DNA and various proteins. Furthermore, since the immobilization force is dominated by the dielectrophoresis force, it can potentially be tuned according to particle size and material properties. In addition, the well-understood surface chemistry41 of gold nanocrystals makes them ideal carriers of other materials such as DNA, therefore, NanoPen patterning of gold nanoparticles can be used to pattern other materials conjugated to the gold surface. In its present form NanoPen introduces a flexible, real-time reconfigurable, large-scale, and low-power method for patterning various nanostructures with potential applications in chemical and biological sensing, opto- and nano-electronic device fabrication, nanostructure synthesis, and photovoltaics.

Supplementary Material


This work was supported in part by DARPA SERS S&T Fundamentals #FA9550-08-1-0257 (Dr. Dennis Polla) and the National Institutes of Health through the NIH Roadmap for Medical Research (Grant #PN2 EY018228). The authors would like to thank Professor Peidong Yang, Professor Luke P. Lee, Dr. Yeonho Choi, Amit Lakhani and Tae Joon Seok for valuable discussions and comments. PJP thanks the Lawrence Livermore National Laboratory for support through the Lawrence post-doctoral fellowship.


Supporting Information Available: Extensive figures on patterning a single Au nanoparticle, NanoPen patterning of 1-dimensional structures such as multi-wall carbon nanotubes and nanowires, Patterning of nanoparticles with various surface charges, Analysis of nanoparticle concentration in NanoPen patterned structures, and SERS detection of 10 pM concentration BPE molecules using NanoPen patterned Au nanoparticle structures. This material is available free of charge via the Internet at


1. Brown PO, Botstein D. Nat. Genet. 1999;21:33–37. [PubMed]
2. Schena M, Shalon D, Davis RW, Brown PO. Science. 1995;270:467–470. [PubMed]
3. Anker JN, Hall WP, Lyandres O, Shah NC, Zhao J, Van Duyne RP. Nat. Mater. 2008;7:442–453. [PubMed]
4. Huang MH, Mao S, Feick H, Yan H, Wu Y, Kind H, Weber E, Russo R, Yang P. Science. 2001;292:1897–1899. [PubMed]
5. Javey A, Guo J, Wang Q, Lundstrom M, Dai H. Nature. 2003;424:654–657. [PubMed]
6. Yang P. MRS Bull. 2005;30:85–91.
7. Sun B, Findikoglu AT, Sykora M, Werder DJ, Klimov VI. Nano Lett. 2009;9:1235. [PubMed]
8. Piner RD, Zhu J, Xu F, Hong S, Mirkin CA. Science. 1999;283:661–663. [PubMed]
9. Salaita K, Wang Y, Mirkin CA. Nat. Nanotechnol. 2007;145:145–155. [PubMed]
10. Basnar B, Willner I. Small. 2009;5:28. [PubMed]
11. Ginger DS, Zhang H, Mirkin CA. Angew. Chem. Int., Ed. 2004;43:30. [PubMed]
12. Li B, Goh CF, Zhou X, Lu G, Tantang H, Chen Y, Xue C, Boey FYC, Zhang H. Adv. Mater. 2008;20:4873–4878.
13. Wang HT, Nafday OA, Haaheim JR, Tevaarwerk E, Amro NA, Sanedrin RG, Chang CY, Ren F, Pearton SJ. Appl. Phys. Lett. 2008;93:143105.
14. Hulteen JC, Treichel DA, Smith MT, Duval ML, Jensen TR, Van Duyne RP. J. Phys. Chem. B. 1999;103:3854–3863.
15. Ahn JH, Kim HS, Lee KJ, Jeon S, Kang SJ, Sun Y, Nuzzo RG, Rogers JA. Science. 2006;314:1754–1757. [PubMed]
16. Fan Z, Ho JC, Jacobson ZA, Yerushalmi R, Alley RL, Razavi H, Javey A. Nano Lett. 2008;8:20–25. [PubMed]
17. He HX, Li QG, Zhou ZY, Zhang H, Huang W, Li SFY, Liu ZF. Langmuir. 2000;16:9683.
18. Xia Y, Whitesides GM. Annu. Rev. Mater. Sci. 1998;28:153.
19. Yerushalmi R, Ho JC, Jacobson ZA, Javey A. Nano Lett. 2007;7:2764–2768. [PubMed]
20. Rabani E, Reichman DR, Geissler PL, Brus LE. Nature. 2003;426:271–274. [PubMed]
21. Collier CP, Saykally RJ, Shiang JJ, Henrichs SE, Heath JR. Science. 1997;277:1978–1981.
22. Hayward RC, Saville DA, Aksay IA. Nature. 2000;404:56–59. [PubMed]
23. Williams SJ, Kumar A, Wereley ST. Lab Chip. 2008;8:1879–1882. [PubMed]
24. Pauzauskie PJ, Radenovic A, Trepagnier E, Shroff H, Yang PD, Liphardt J. Nat. Mater. 2006;5:97–101. [PubMed]
25. Ito S, Yoshikawa H, Masuharaa H. Appl. Phys. Lett. 2001;78:2566–2568.
26. Wilson BK, Hegg M, Miao X, Cao G, Lin LY. Opt. Express. 2008;16:17276–17281. [PubMed]
27. Chiou PY, Ohta AT, Wu MC. Nature. 2005;436:370–372. [PubMed]
28. Jones TB. Electromechanics of Particles. Cambridge University Press; Cambridge: 1995.
29. Ohta AT, Chiou PY, Phan HL, Sherwood SW, Yang JM, Lau ANK, Hsu HY, Jamshidi A, Wu MC. IEEE J. Sel. Top. Quantum Electron. 2007;243:235–243.
30. Jamshidi A, Pauzauskie PJ, Schuck PJ, Ohta AT, Chiou PY, Chou J, Yang PD, Wu MC. Nat. Photonics. 2008;2:85–89. [PMC free article] [PubMed]
31. Valley JK, Jamshidi A, Ohta AT, Hsu HY, Wu MC. J. Microelectromech. Syst. 2008;17:342–350. [PMC free article] [PubMed]
32. Chiou PY, Ohta AT, Jamshidi A, Hsu HY, Wu MC. J. Microelectromech. Syst. 2008;17:525.
33. Ramos A, Morgan H, Green NG, Castellanos A. J. Colloid Interface Sci. 1999;217:420–422. [PubMed]
34. Castellanos A, Ramos A, Gonzalez A, Green NG, Morgan H. J. Phys. D: Appl. Phys. 2003;36:2584–2597.
35. Ramos A, Morgan H, Green NG, Castellanos A. J. Phys. D: Appl. Phys. 1998;31:2338–2353.
36. Lyklema J. Fundamentals of Interface and Colloid Science. Vol. 2. Academic; Academic; London, U.K.: 1991.
38. Yang W, Hulteen J, Schatz GC, Van Duyne RP. J. Chem. Phys. 1996;104:4313–4323.
39. Tien MC, Ohta AT, Yu K, Neale SL, Wu MC. Appl. Phys. A: Mater. Sci. Process. 2009;95:967.
40. Psaltis D, Quake SR, Yang C. Nature. 2006;442:381–386. [PubMed]
41. Daniel MC, Astruc D. Chem. Rev. 2004;104:293–346. [PubMed]